Multimodal ethylene-based polymer processing systems and methods

ABSTRACT

Embodiments of methods for producing a trimodal polymer in a solution polymerization process comprise three solution polymerization reactors organized in parallel or in series.

CROSS REFERENCE TO RELATED APPLICATION

This application claims priority to U.S. Provisional Application Ser. No. 62/610,383, filed Dec. 26, 2017, which is hereby incorporated by reference in its entirety.

TECHNICAL FIELD

Embodiments of the present disclosure generally relate to systems and methods for multimodal ethylene-based polymer processing. More specifically, embodiments of the present disclosure relate to reactor configurations and methods of using these configurations to produce polymers, in particular, multimodal ethylene-based polymers (e.g., trimodal polymers).

BACKGROUND

Polyethylene is one of the most common plastics and may be used in a variety ways depending on the structure of the polymer, for example, bags/liners, caps/closures, hygiene films, industrial injection molding, etc. It has been estimated that approximately 80 million tons of polyethylene is produced each year. In order to meet demand as well as provide new polymer structures with useful properties, it is necessary to provide new polymer processing systems and methods.

Particularly useful polyethylene structures are multimodal ethylene-based polymers, e.g., trimodal polymers, because they may combine the processability of resin with a balance of desirable properties such as strength, barrier properties, etc. However, the production of multimodal ethylene-based polymers is still challenging and problematic as gelling, especially for the high molecular weight component, process control, and other issues may arise. Accordingly, there is a continual need for improved processes for making multimodal ethylene-based polymers.

SUMMARY

Embodiments of the present disclosure address the needs discussed above by including a system having three solution polymerization reactors, one of which is an adiabatic reactor. The adiabatic reactor may produce a high molecular weight component for the multimodal ethylene-based polymer, while ensuring the viscosity is maintained at a manageable level such that gelling is prevented.

According to one embodiment, a method of producing a trimodal polymer in a solution polymerization process is provided. The method comprises introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a first solution polymerization reactor to produce an effluent comprising a first ethylene-based component, wherein the first ethylene-based component has a density (ρ₁) as measured according to ASTM D792, and a weight-average molecular weight (M_(w(GPC),1)) as measured according to Gel Permeation Chromatography (GPC). Additionally, the method comprises introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a second solution polymerization reactor downstream from the first solution polymerization reactor to produce an effluent comprising the first ethylene-based component and a second ethylene-based component, wherein the second ethylene-based component has a density (ρ₂), and a weight-average molecular weight (M_(w(GPC),2)) Further, the method comprises introducing the first ethylene-based component, the second ethylene-based component, at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a third solution polymerization reactor downstream from the second solution polymerization reactor to produce an effluent comprising the trimodal polymer, wherein the trimodal polymer comprises the first ethylene-based component, the second ethylene-based component, and a third ethylene-based component, wherein the third ethylene-based component has a density (ρ₃), and a weight-average molecular weight (M_(w(GPC),3)). Moreover, the first solution polymerization reactor or the third polymerization reactor is an adiabatic reactor, and each of ρ₁, ρ₂, and ρ₃ have different densities and each of M_(w(GPC),1), M_(w(GPC)2), and M_(w(GPC),3) have different weight-average molecular weights.

According to yet another method of producing a trimodal polymer in a solution polymerization process, the method comprises introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a first solution polymerization reactor to produce an effluent comprising a first ethylene-based component, wherein the first ethylene-based component has a density (ρ₁) as measured according to ASTM D792, and a weight-average molecular weight (M_(w(GPC),1)) as measured according to Gel Permeation Chromatography (GPC). Further, the method comprises introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen in the second solution polymerization reactor to produce an effluent comprising a second ethylene-based component, wherein the second ethylene-based component has a density (ρ₂), and a weight-average molecular weight (M_(w(GPC),2)) Additionally, the method comprises introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to the third solution polymerization reactor to produce an effluent comprising a third ethylene-based component, wherein the third ethylene-based component has a density (ρ₃), and a weight-average molecular weight (M_(w(GPC),3)) Further, the method comprises mixing the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component to produce the trimodal polymer. Moreover, the first solution polymerization reactor or the third polymerization reactor is an adiabatic reactor, and each of ρ₁, ρ₂, and ρ₃ have different densities and each of M_(w(GPC),1), M_(w(GPC),2), and M_(w(GPC),3) have different weight-average molecular weights.

BRIEF DESCRIPTION OF THE DRAWINGS

The following detailed description of specific embodiments of the present disclosure can be best understood when read in conjunction with the drawings enclosed herewith.

FIG. 1 is a schematic depiction of a series reactor system configuration in accordance with one or more embodiments of the present disclosure.

FIG. 2 is a schematic depiction of a parallel reactor system configuration in accordance with one or more embodiments of the present disclosure.

FIG. 3 is a graphical illustration of a Crystallization Elution Fractionation (CEF) overlay.

For the purpose of describing the simplified schematic illustrations and descriptions of FIGS. 1 and 2, the numerous valves, heat exchangers, agitators, temperature sensors, electronic controllers and the like that may be employed and are well known to those of ordinary skill in the art of certain chemical processing operations are not included. It should be understood that these components are within the spirit and scope of the present embodiments disclosed.

It should be understood that two or more process streams are “mixed”, “combined” or “split” when two or more lines intersect or meet at a junction in the schematic flow diagrams of FIGS. 1 and 2. Mixing or combining may also include mixing by directly introducing both streams into a like reactor, separation device, or other system component. For example, it should be understood that when two streams are depicted as being combined directly prior to entering a reactor, that in some embodiments the streams could equivalently be introduced into the reactor and be mixed in the reactor.

DETAILED DESCRIPTION Definitions

The term “polymer” refers to a polymeric compound prepared by polymerizing monomers, whether of the same or a different type. The generic term polymer thus embraces the term “homopolymer,” usually employed to refer to polymers prepared from only one type of monomer as well as “copolymer,” which refers to polymers prepared from two or more different monomers. The term “interpolymer,” as used herein, refers to a polymer prepared by the polymerization of at least two different types of monomers. The generic term interpolymer thus includes copolymers, and polymers prepared from more than two different types of monomers, such as terpolymers.

“Polyethylene” or “ethylene-based polymer” shall mean polymers comprising greater than 50% by weight of units which have been derived from ethylene monomer. This includes polyethylene homopolymers or copolymers (meaning units derived from two or more comonomers). Common forms of polyethylene known in the art include Low Density Polyethylene (LDPE); Linear Low Density Polyethylene (LLDPE); Ultra Low Density Polyethylene (ULDPE); Very Low Density Polyethylene (VLDPE); single-site catalyzed Linear Low Density Polyethylene, including both linear and substantially linear low density resins (m-LLDPE); Medium Density Polyethylene (MDPE); and High Density Polyethylene (HDPE).

As used herein, “multimodal” means compositions that can be characterized by having at least three polymer subcomponents with varying densities and weight-average molecular weights, and optionally, may also have different melt index values. In one embodiment, multimodal may be defined by having at least three distinct peaks in a Gel Permeation Chromatography (GPC) chromatogram showing the molecular weight distribution. In another embodiment, multimodal may be defined by having at least three distinct peaks in a Crystallization Elution Fractionation (CEF) chromatogram showing the short chain branching distribution. Multimodal includes resins having three peaks as well as resins having more than three peaks.

The term “trimodal polymer” means a multimodal ethylene-based polymer having three primary components: a first ethylene-based polymer component, a second ethylene-based polymer component, and a third ethylene-based polymer component.

“Polyethylene component”, for example, the “first ethylene-based component”, the “second ethylene-based component”, or the “third ethylene-based component” refer to subcomponents of the multimodal or trimodal polymer, wherein each subcomponent is an ethylene interpolymer comprising ethylene monomer and C₃-C₁₂ α-olefin comonomer.

As used herein, the term “adiabatic reactor” refers to a solution polymerization reactor or vessel operating without the addition or removal of heat. Consequently, the “adiabatic reactor” may be a reactor not coupled to or in communication with a heat exchanger.

As used herein, the “solution polymerization reactor” is a vessel, which performs solution polymerization, wherein ethylene monomer and at least C₃-C₁₂ α-olefin comonomer copolymerize after being dissolved in a non-reactive solvent that contains a catalyst. In the solution polymerization process, hydrogen may be utilized; however, it is not required in all solution polymerization processes.

System Embodiments

In some embodiments, the disclosure provides for system having at least three reactors for producing multimodal ethylene-based polymers, wherein the systems provide additional control in producing specific types of polymers, in particular, trimodal polymers.

An example of a reactor system utilizing three reactors in series is shown in FIG. 1. As shown in FIG. 1, the three reactors may comprise a first solution polymerization reactor 101 followed sequentially by a second solution polymerization reactor 102 and a third solution polymerization reactor 103. In one or more embodiments, the first solution polymerization reactor 101 or the third polymerization reactor 103 is an adiabatic reactor. In a further embodiment, the first solution polymerization reactor 101 is an adiabatic reactor.

In certain methods, which utilize the three reactor configuration disclosed in FIG. 1, it is possible to produce, among other things, a multimodal ethylene-based polymer, specifically a trimodal polymer. One method of producing a trimodal polymer in the reactor system 1 of FIG. 1 involves introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen in the first solution polymerization reactor 101 to produce an effluent 20 comprising a first ethylene-based component. The feed to the reactor is depicted as two streams 10 and 11, where stream 10 is the feed of monomer and C₃-C₁₂ α-olefin comonomer and stream 11 is the feed of catalyst/cocatalyst and solvent. However, it is contemplated that more or less feed inlets may be used.

Referring again to FIG. 1, the effluent 20 comprising the first ethylene-based component is then transferred to the second solution polymerization reactor 102 along with at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen. The second solution polymerization reactor 102 reacts the materials together to produce an effluent 30 comprising the first ethylene-based component, and a second ethylene-based component. The effluent 30 comprising the second ethylene-based component is then transferred to the third solution polymerization reactor 103 along with at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen.

The third solution polymerization reactor 103 then mixes the materials together to produce an effluent comprising the first and second ethylene-based components as well as the third ethylene-based component, wherein these three ethylene-based polymer components make up the trimodal polymer.

When the reactor system shown in FIG. 1 is connected in series, the first solution polymerization reactor 101 may operate at the same pressure as the second solution polymerization reactor 102 and/or the third solution polymerization reactor 103. In one embodiment, all three reactors 101,102,103 may operate at the same pressure. To this end, the reactors may be configured to minimize pressure drop between each other.

As an alternative to the three reactor series embodiment depicted in FIG. 1, it is possible for a parallel three reactor system as shown in FIG. 2. As shown in FIG. 2, a first solution polymerization reactor 101 may receive a monomer feed 11, a catalyst, a solvent feed 10, and optionally hydrogen. These inlets may be further separated or combined depending on the system. In the first solution polymerization reactor 101, the at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen react to produce an effluent 20 comprising the first ethylene-based component. In the embodiment of FIG. 2, the feed may be split into multiple streams for example, 121, 122, and 123. In other embodiments, the effluent 20 is not split into multiple streams and thus substantially the entire effluent is fed to the second solution polymerization reactor 102, and/or the third polymerization reactor 103, which operates in parallel to the second solution polymerization reactor 102.

Referring again to an embodiment depicted in FIG. 2, the effluent 121 comprising the first ethylene-based component is passed to the second solution polymerization reactor 102, wherein the first ethylene-based component is mixed with at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to produce an effluent 130 comprising the first ethylene-based component and a second ethylene-based component. While not shown in FIGS. 1 and 2, the feed components (catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer) may be fed separately from the feeds of the second solution polymerization reactor 102 and the third solution polymerization reactor 103.

Referring again to FIG. 2, the effluent 122, which comprises the first ethylene-based component, may also be passed to the third solution polymerization reactor 103. Within the third solution polymerization reactor 103, the first ethylene-based component, the catalyst, ethylene monomer, the C₃-C₁₂ α-olefin comonomer, the solvent, and optionally the hydrogen react to produce an effluent 135 comprising the first ethylene-based component and a third ethylene-based component. The effluents produced by the second polymerization reactor 102 and the third polymerization reactor 103 are then mixed together to produce a trimodal polymer 40. This is depicted at junction 112; however, other mixing locations and are contemplated. Additionally, in a further embodiment, at least a portion 132 of the effluent 130 from the first polymerization reactor 102 may be passed to the second polymerization reactor 103. In specific embodiment, the effluent stream may be split at junction 114, which may represent a flow splitter.

Various temperature conditions are contemplated for three solution polymerization reactors. For example, the temperatures of the reactors may be in the range from 115 to 215° C. The reactor temperatures for each may be varied based on the final trimodal polymer sought.

In some embodiments, the systems of FIGS. 1 and 2 may comprise a tubular reactor 104, which allows for further reaction and conversion of the trimodal polymer 104. In general, the tubular reactor 104 provides additional conversion of the components of the trimodal polymer by increasing the residence time. Moreover, the tubular reactor 104 may improve catalyst efficiency by allowing the reactors to run at higher ethylene concentrations and reducing energy consumption by raising the polymer temperature and thereby reducing the heat input required before a solvent removal step. Various reactors are considered suitable and would be familiar to one of ordinary skill in the art.

Additional process steps can be included in the systems of FIGS. 1 and 2, for example, catalyst kill steps. Catalyst kill steps may involve the addition of a polar compound to deactivate the polymerization catalysts. Suitable polar compounds used as catalyst kill agents may include water, polyethylene glycol, butylated hydroxytoluene (BHT), glycerol, or combinations thereof

Other process flows and alterations, as would be recognized by a person of ordinary skill in the art, are within the scope of FIGS. 1 and 2.

Trimodal Polymer

As stated above, the yield of the systems depicted in FIGS. 1 and 2 is a trimodal polymer, which as stated above is an example of a multi-modal ethylene-based polymer. In certain embodiments of the trimodal polymer, the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component may be defined by density (ρ₁, ρ₂, and ρ₃, respectively), weight average molecular weight (M_(w(GPC),1), M_(w(GPC),2), and M_(w(GPC),3), respectively), and/or melt index (MI₁, MI₂, and MI₃, respectively).

For the trimodal polymer, the densities (ρ₁, ρ₂, and ρ₃) for the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component, respectively, may each have different density values. Similarly, the weight-average molecular weights (M_(w(GPC),1), M_(w(GPC),2), and M_(w(GPC),3)) may each have different weight-average molecular weight values. Without being bound by theory, the variance in densities and molecular weights between the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component enables the trimodal polymer to have a desired combination of strength and processibility.

In further embodiments, the trimodal polymer may be defined such that ρ₁ is less than ρ₂ and is also less than ρ₃ and wherein M_(w(GPC),1) is greater than M_(w(GPC),2) and is also greater than M_(w(GPC),3). In further embodiments, MI₁ is less than MI₂ and MI₁ is also less than MI₃. In one embodiment, the final product may be defined such that ρ₁<ρ₂<ρ₃, and M_(w(GPC),3)>M_(w(GPC),2)>M_(w(GPC),1). In such an embodiment, the first ethylene-based component may be considered as the low density component, the second ethylene-based component may be considered as the intermediate density component, the third ethylene-based component may be considered the high density component. In order to achieve such distributions, the catalyst in the first solution polymerization reactor may differ from the catalyst used in the second solution polymerization reactor and the catalyst used in the third solution polymerization reactor. In other embodiments, the distribution may be achieved by using a different catalyst in each of the first solution polymerization reactor, the second solution polymerization reactor, and the third solution polymerization reactor. In yet another embodiment, the melt index of the trimodal polymer may be defined as follows: MI₁<MI₂<MI₃.

In one or more embodiments, densities of the first ethylene-based component (ρ₁), the second ethylene-based component (ρ₂), and the third ethylene-based component (ρ₃) may be 0.855 g/cc to 0.935 g/cc, 0.885 to 0.945 g/cc, and 0.900 to 0.980 g/cc, respectively. In further embodiments, the first ethylene-based component may have a density (ρ₁) from 0.865 g/cc to 0.920 g/cc, or from 0.870 to 0.910 g/cc. Moreover, the second ethylene-based component may have a density (ρ₂) from 0.890 g/cc to 0.930 g/cc, or from 0.895 g/cc to 0.925 g/cc. Further, the third ethylene-based component may have a density (ρ₃) from 0.920 g/cc to 0.980 g/cc, or from 0.935 g/cc to 0.9670 g/cc. In some embodiments, the final density of the trimodal polymer may be from 0.900 g/cc to 0.960 g/cc, or from 0.905 g/cc to 0.950 g/cc, or from 0.910 g/cc to 0.940 g/cc.

In one or more embodiments, the weight average molecular weights of the first ethylene-based component (M_(w(GPC),1)), the second ethylene-based component (M_(w(GPC),2)), and the third ethylene-based component (M_(w(GPC),3)) are 90 kg/mol to 500 kg/mol, 70 kg/mol to 300 kg/mol, and 10 kg/mol to 170 kg/mol, respectively. In further embodiments, the first ethylene-based component may have a weight average molecular weight (M_(w(GPC),1)) of 100 kg/mol to 363 kg/mol, or from 150 kg/mol to 350 kg/mol. Moreover, in further embodiments, the second ethylene-based component may have a weight average molecular weight (M_(w(GPC),2)) of 100 kg/mol to 200 kg/mol, or from 110 kg/mol to 190 kg/mol, or from 120 kg/mol to 175 kg/mol, or from 120 kg/mol to 170 kg/mol. Furthermore, in additional embodiments, the third ethylene-based component may have a weight average molecular weight (M_(w(GPC),3)) of 15 kg/mol to 160 kg/mol, or from 16 kg/mol to 120 kg/mol, or from 17 kg/mol to 90 kg/mol, or from 18 kg/mol to 60 kg/mol.

Similarly, in some embodiments, the first ethylene-based component has a melt index (MI_(i)) of from 0.001 g/10 min to 1.0 g/10 min, or from 0.01 g/10 min to 0.5 g/10 min, or from 0.01 g/10 min to 0.1 g/10 min. Moreover, the second ethylene-based component may have a melt index (MI₂) of from 0.01 g/10 min to 2.0 g/10 min, or from 0.1 g/10 min to 1.0 g/10 min, or from 0.2 g/10 min to 0.7 g/10 min. Further, the third ethylene-based component may have a melt index (MI₃) of from 0.1 g/10 min to 5000 g/10 min, or from 0.5 g/10 min to 4000 g/10 min, or from 1 g/10 min to 3000 g/10 min, or from 10 g/10 min to 1000 g/10 min, or from 50 g/10 min to 750 g/10 min. In further embodiments, the trimodal polymer has a melt index (I₂) of from 0.1 g/10 min to 10.0 g/10 min, or from 0.2 to 5.0 g/10 min, or from 0.5 to 1.0 g/10 min.

Various amounts are contemplated for the components of the trimodal polymer. In one or more embodiments, the trimodal polymer may comprise from 2 to 45% by weight of the first ethylene-based component, or from 20 to 45% by weight of the first ethylene-based component, or from or from 25 to 45% by weight of the first ethylene-based component. Moreover, the trimodal polymer may comprise from 2 to 40% by weight of the second ethylene-based component, or from 5 to 40% by weight of the second ethylene-based component, or from or from 10 to 35% by weight of the second ethylene-based component. Moreover, the trimodal polymer may comprise from 30 to 70% by weight of the third ethylene-based component, or from 35 to 65% by weight of the third ethylene-based component, or from 40 to 60% by weight of the third ethylene-based component, or from 45 to 55% by weight of the third ethylene-based component.

Reactors

Various embodiments are contemplated for the first, second and third solution polymerization reactors. As stated above, at least one of the first, second, and third solution polymerization reactors is an adiabatic reactor. In specific embodiments, the first solution polymerization reactor is an adiabatic reactor.

Various vessels are contemplated for use as the adiabatic reactor. In one or more embodiments, the adiabatic reactor may comprise a static mixer, a mechanical mixer, or a continuous stirred tank reactor (CSTR). In a specific embodiment, the first solution polymerization reactor 101 may be a continuous stirred tank reactor (CSTR). While various reactor sizes are contemplated, in some embodiments, the first solution polymerization reactor 101 may be half or less than half of the volume of the second solution polymerization reactor 102 and/or the third solution polymerization reactor 103. While the first solution polymerization reactor 101 is discussed herein for producing the first ethylene-based component, it is contemplated that the first solution polymerization reactor 101 could be used for the other polyethylene components.

These may include conventional reactors such as loop reactors, spherical reactors, isothermal reactors, stirred tank reactors, batch reactors, or any combinations thereof. In one embodiment, the second solution polymerization reactor 102, the third solution polymerization reactor 103, or both may include loop reactors. Moreover, the second solution polymerization reactor 102, the third solution polymerization reactor 103, or both may each include single reactor vessels, or multiple reactors in series or parallel. In one or more embodiments, a two loop vessels or three loop vessels may be used for the second solution polymerization loop reactor 102, the third solution polymerization loop reactor 103, or both.

In a specific embodiment, the first solution polymerization reactor 101 is an adiabatic continuous stirred tank reactor, while the second solution polymerization reactor 102 and the third solution polymerization reactor 103 are loop reactors.

In further embodiments, the first and second solution polymerization loop reactors may comprise one or more pumps (not shown). A pump may transport at least a portion of a reaction stream at least a portion of the way around a flow loop. For example, a pump may transport at least a portion of a reaction stream from a heat exchanger to a product outlet.

Moreover, each loop reactor may comprise one or more heat exchangers (not shown) and, optionally, pipes connecting them to each other and/or to the remainder of the reactor, according to some embodiments. A flow loop may be configured, in some embodiments, with or without interconnecting pipes between components. In some embodiments, it may be desirable to configure every element along the flow path to act as a reaction zone. In such embodiments, the regions where heat transfer takes place may be maximized at the expense of connecting pipes where the transfer is minimal or non-existent. A heat exchanger may comprise, in some embodiments, at least one cooling fluid inlet and at least one cooling fluid outlet. According to some embodiments, a heat exchanger may further comprise at least one reaction stream inlet and at least one reaction stream outlet. In some embodiments, any heat exchange apparatus may be used, in any configuration. For example, a heat exchanger may include a cooling coil positioned in a flow loop. In another example, a heat exchanger may include a shell-and-tube heat exchanger positioned in a flow loop wherein the flow stream passes through the tubes. In another example, an entire flow loop may be configured as a heat exchanger by enclosing it in a cooling jacket or double piping.

Feed Components

Various embodiments are contemplated for the C₃-C₁₂ comonomer, solvent, and catalysts.

In some embodiments, the C₃-C₁₂ α-olefin comonomer is propene, butene, pentene, hexene, pentene, octene, nonene, decene, undecene, dodecene, or combinations thereof. In specific embodiments, the C₃-C₁₂ α-olefin comonomer is octene. It is contemplated that the same C₃-C₁₂ α-olefin comonomer is used in all three reactors. Alternatively, it is contemplated that the C₃-C₁₂ α-comonomer may differ in the three reactor systems depicted in FIGS. 1 and 2.

Various solvents are considered suitable for use in the adiabatic reactor, and the first and second solution polymerization reactors. The solvents may vary based on the catalyst used in the specific reactors. Solvents may include, for example, paraffinic/isoparaffinic solvents, olefinic solvents, aromatic solvents, cyclic solvents, and combinations thereof. Exemplary solvents include, but are not limited to, isoparaffins. For example, such isoparaffin solvents are commercially available under the name ISOPAR E from ExxonMobil Chemical.

Catalysts

As stated above, the catalysts may vary between adiabatic reactors and solution polymerization reactors in order to impart different properties to the first ethylene-based component, the second ethylene-based component and third ethylene-based component.

Various catalysts are considered suitable. These may include, but are not limited to, a Ziegler-Natta catalyst, a chromium catalyst, a metallocene catalyst, a post-metallocene catalyst, a constrained geometry complex (CGC) catalyst, a phosphinimine catalyst, or a bis(biphenylphenoxy) catalyst. Details and examples of CGC catalysts are provided in U.S. Pat. Nos. 5,272,236; 5,278,272; 6,812,289; and WO Publication 93/08221, which are all incorporated herein by reference in their entirety. Details and examples of bis(biphenylphenoxy) catalysts are provided in U.S. Pat. Nos. 6,869,904; 7,030,256; 8,101,696; 8,058,373; 9,029,487, which are all incorporated herein by reference in their entirety. The catalysts utilized in the solution polymerization reactors may vary in order to impart different properties to the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component. For example, it is contemplated to use different catalysts in the first, second and third solution polymerization reactors to vary the density, melt index, comonomer incorporation, etc. of the first, second, and third ethylene-based components. Without being bound by theory, varying these parameters for the first, second, and third ethylene-based components may enable the multimodal ethylene-based polymer to have a desired combination of toughness and processability.

In one or more embodiments, the first solution polymerization reactor, the second solution polymerization reactor, and/or the third solution polymerization reactor may include homogenous or heterogeneous catalysts. Homogeneous, often referred to as single-site, catalysts are organometallic compounds which typically have a discrete molecular structure, and are used to generate polymers, which have narrow molecular weight distribution, as well as narrow composition distribution, in the case where interpolymers are made. Homogeneous catalysts may be dissolved in a solution process or supported for use in particle forming processes, such as slurry or gas phase. Heterogeneous catalysts are not discrete compounds but rather result from a reaction mixture of metal compounds with precursors to form a complex, which has multiple active sites on some form of a particle. Polymers produced via heterogeneous catalysts typically demonstrate broader molecular weight distributions and, in the case of interpolymers, broader composition distributions than homogeneous catalysts.

The bis(biphenylphenoxy) catalyst is an example of a homogeneous catalyst. Other examples of homogeneous catalysts include constrained geometry catalysts. Examples of heterogeneous catalysts may include Ziegler-Natta catalysts, which are particularly useful at the high polymerization temperatures of the solution process. Examples of such Ziegler-Natta catalysts are those derived from organomagnesium compounds, alkyl halides or aluminum halides or hydrogen chloride, and a transition metal compound. Examples of such catalysts are described in U.S. Pat. No. 4,314,912 (Lowery, Jr. et al.), U.S. Pat. No. 4,547,475 (Glass et al.), and U.S. Pat. No. 4,612,300 (Coleman, III), the teachings of which are incorporated herein by reference.

Particularly suitable organomagnesium compounds include, for example, hydrocarbon soluble dihydrocarbylmagnesium such as the magnesium dialkyls and the magnesium diaryls. Exemplary suitable magnesium dialkyls include particularly n-butyl-secbutylmagnesium, diisopropylmagnesium, di-n-hexylmagnesium, isopropyl-n-butyl-magnesium, ethyl-n-hexylmagnesium, ethyl-n-butylmagnesium, di-n-octylmagnesium and others wherein the alkyl has from 1 to 20 carbon atoms. Exemplary suitable magnesium diaryls include diphenylmagnesium, dibenzylmagnesium and ditolylmagnesium. Suitable organomagnesium compounds include alkyl and aryl magnesium alkoxides and aryloxides and aryl and alkyl magnesium halides with the halogen-free organomagnesium compounds being more desirable.

Bis(biphenylphenoxy) catalysts are multi-component catalyst systems comprising a bis(biphenylphenoxy) procatalyst, cocatalyst, as well as further optional ingredients. The bis(biphenylphenoxy) procatalyst may include a metal-ligand complex according to Formula (I):

In Formula (I), M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4; n is 0, 1, or 2; when n is 1, X is a monodentate ligand or a bidentate ligand; when n is 2, each X is a monodentate ligand and is the same or different; the metal-ligand complex is overall charge-neutral; O is O (an oxygen atom); each Z is independently chosen from —O—, —S—, —N(R^(N))—, or P(R^(P))—; L is (C₁-C₄₀)hydrocarbylene or (C₁-C₄₀)heterohydrocarbylene, wherein the (C₁-C₄₀)hydrocarbylene has a portion that comprises a 1-carbon atom to 10-carbon atom linker backbone linking the two Z groups in Formula (I) (to which L is bonded) or the (C₁-C₄₀)heterohydrocarbylene has a portion that comprises a 1-atom to 10-atom linker backbone linking the two Z groups in Formula (I), wherein each of the 1 to 10 atoms of the 1-atom to 10-atom linker backbone of the (C₁-C₄₀)heterohydrocarbylene independently is a carbon atom or heteroatom, wherein each heteroatom independently is O, S, S(O), S(O)₂, Si(R^(C))₂, Ge(R^(C))₂, P(R^(C)), or N(R^(C)), wherein independently each R^(C) is (C₁-C₃₀)hydrocarbyl or (C₁-C₃₀)heterohydrocarbyl; R¹ and R⁸ are independently selected from the group consisting of (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, and radicals having Formula (II), Formula (III), or Formula (IV):

In Formulas (II), (III), and (IV), each of R³¹⁻³⁵, R⁴¹⁻⁴⁸, or R⁵¹⁻⁵⁹ is independently chosen from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, or —H, provided at least one of R¹ or R⁸ is a radical having Formula (II), Formula (III), or Formula (IV).

In Formula (I), each of R²⁻⁴, R⁵⁻⁷, and R⁹⁻¹⁶ is independently selected from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂—OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(C))₂NC(O)—, halogen, and —H.

Specific embodiments of catalyst systems will now be described. It should be understood that the catalyst systems of this disclosure may be embodied in different forms and should not be construed as limited to the specific embodiments set forth in this disclosure. Rather, embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the subject matter to those skilled in the art.

The term “independently selected” is used herein to indicate that the R groups, such as, R¹, R², R³, R⁴, and R⁵ can be identical or different (e.g., R¹, R², R³, R⁴, and R⁵ may all be substituted alkyls or R¹ and R² may be a substituted alkyl and R³ may be an aryl, etc.). Use of the singular includes use of the plural and vice versa (e.g., a hexane solvent, includes hexanes). A named R group will generally have the structure that is recognized in the art as corresponding to R groups having that name. These definitions are intended to supplement and illustrate, not preclude, the definitions known to those of skill in the art.

The term “procatalyst” refers to a compound that has catalytic activity when combined with an activator. The term “activator” refers to a compound that chemically reacts with a procatalyst in a manner that converts the procatalyst to a catalytically active catalyst. As used herein, the terms “cocatalyst” and “activator” are interchangeable terms.

When used to describe certain carbon atom-containing chemical groups, a parenthetical expression having the form “(C_(x)C_(y))” means that the unsubstituted form of the chemical group has from x carbon atoms to y carbon atoms, inclusive of x and y. For example, a (C₁-C₄₀)alkyl is an alkyl group having from 1 to 40 carbon atoms in its unsubstituted form. In some embodiments and general structures, certain chemical groups may be substituted by one or more substituents such as R^(S). An R^(S) substituted version of a chemical group defined using the “(C_(x)C_(y))” parenthetical may contain more than y carbon atoms depending on the identity of any groups R^(S). For example, a “(C₁-C₄₀)alkyl substituted with exactly one group R^(S), where R^(S) is phenyl (C₆H₅)” may contain from 7 to 46 carbon atoms. Thus, in general when a chemical group defined using the “(C_(x)C_(y))” parenthetical is substituted by one or more carbon atom-containing substituents R^(S), the minimum and maximum total number of carbon atoms of the chemical group is determined by adding to both x and y the combined sum of the number of carbon atoms from all of the carbon atom-containing substituents R^(S).

In some embodiments, each of the chemical groups (e.g., X, R, etc.) of the metal ligand complex of Formula (I) may be unsubstituted having no R^(S) substituents. In other embodiments, at least one of the chemical groups of the metal-ligand complex of Formula (I) may independently contain one or more than one R^(S). In some embodiments, the sum total of R^(S) in the chemical groups of the metal-ligand complex of Formula (I) does not exceed 20. In other embodiments, the sum total of R^(S) in the chemical groups does not exceed 10. For example, if each R¹⁻⁵ was substituted with two R^(S), then X and Z cannot be substituted with an R^(S). In another embodiment, the sum total of R^(S) in the chemical groups of the metal-ligand complex of Formula (I) may not exceed 5 R^(S). When two or more than two R^(S) are bonded to a same chemical group of the metal-ligand complex of Formula (I), each R^(S) is independently bonded to the same or different carbon atom or heteroatom and may include persubstitution of the chemical group.

The term “substitution” means that at least one hydrogen atom (H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or functional group is replaced by a substituent (e.g. R^(S)). The term “persubstitution” means that every hydrogen atom (H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or functional group is replaced by a substituent (e.g., R^(S)). The term “polysubstitution” means that at least two, but fewer than all, hydrogen atoms bonded to carbon atoms or heteroatoms of a corresponding unsubstituted compound or functional group are replaced by a substituent.

The term “H” means a hydrogen or hydrogen radical that is covalently bonded to another atom. “Hydrogen” and “H” are interchangeable and unless clearly specified, mean the same thing.

The term “(C₁-C₄₀)hydrocarbyl” means a hydrocarbon radical of from 1 to 40 carbon atoms and the term “(C₁-C₄₀)hydrocarbylene” means a hydrocarbon diradical of from 1 to 40 carbon atoms, in which each hydrocarbon radical and each hydrocarbon diradical is aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (including mono- and poly-cyclic, fused and non-fused polycyclic, including bicyclic; 3 carbon atoms or more) or acyclic and is unsubstituted or substituted by one or more R^(S).

In this disclosure, a (C₁-C₄₀)hydrocarbyl can be an unsubstituted or substituted (C₁-C₄₀)alkyl, (C₃-C₄₀)cycloalkyl, (C₃-C₂₀)cycloalkyl-(C₁-C₂₀)alkylene, (C₆-C₄₀)aryl, or (C₆-C₂₀)aryl-(C₁-C₂₀)alkylene. In some embodiments, each of the aforementioned (C₁-C₄₀)hydrocarbyl groups has a maximum of 20 carbon atoms (i.e., (C₁-C₂₀)hydrocarbyl) and other embodiments, a maximum of 12 carbon atoms.

The terms “(C₁-C₄₀)alkyl” and “(C₁-C₁₈)alkyl” mean a saturated straight or branched hydrocarbon radical of from 1 to 40 carbon atoms or from 1 to 18 carbon atoms, respectively, which is unsubstituted or substituted by one or more R^(S). Examples of unsubstituted (C₁-C₄₀)alkyl are unsubstituted (C₁-C₂₀)alkyl; unsubstituted (C₁-C₁₀)alkyl; unsubstituted (C₁-C₅)alkyl; methyl; ethyl; 1-propyl; 2-propyl; 1-butyl; 2-butyl; 2-methylpropyl; 1,1-dimethylethyl; 1-pentyl; 1-hexyl; 1-heptyl; 1-nonyl; and 1-decyl. Examples of substituted (C₁-C₄₀)alkyl are substituted (C₁-C₂₀)alkyl, substituted (C₁-C₁₀)alkyl, trifluoromethyl, and [C₄₅]alkyl. The term “[C₄₅]alkyl” (with square brackets) means there is a maximum of 45 carbon atoms in the radical, including substituents, and is, for example, a (C₂₇C₄₀)alkyl substituted by one R^(S), which is a (C₁-C₅)alkyl, respectively. Each (C₁-C₅)alkyl may be methyl, trifluoromethyl, ethyl, 1-propyl, 1-methylethyl, or 1,1-dimethylethyl.

The term “(C₆-C₄₀)aryl” means an unsubstituted or substituted (by one or more R^(S)) mono-, bi- or tricyclic aromatic hydrocarbon radical of from 6 to 40 carbon atoms, of which at least from 6 to 14 of the carbon atoms are aromatic ring carbon atoms, and the mono-, bi- or tricyclic radical comprises 1, 2, or 3 rings, respectively; wherein the 1 ring is aromatic and the 2 or 3 rings independently are fused or non-fused and at least one of the 2 or 3 rings is aromatic. Examples of unsubstituted (C₆-C₄₀)aryl are unsubstituted (C₆-C₂₀) aryl unsubstituted (C₆-C₁₈)aryl; 2-(C₁-C₅)alkyl-phenyl; 2,4-bis(C₁-C₅)alkyl-phenyl; phenyl; fluorenyl; tetrahydrofluorenyl; indacenyl; hexahydroindacenyl; indenyl; dihydroindenyl; naphthyl; tetrahydronaphthyl; and phenanthrene. Examples of substituted (C₆-C₄₀)aryl are substituted (C₁-C₂₀)aryl; substituted (C₆-C₁₈)aryl; 2,4-bis[(C₂₀)alkyl]-phenyl; polyfluorophenyl; pentafluorophenyl; and fluoren-9-one-1-yl.

The term “(C₃-C₄₀)cycloalkyl” means a saturated cyclic hydrocarbon radical of from 3 to 40 carbon atoms that is unsubstituted or substituted by one or more R^(S). Other cycloalkyl groups (e.g., (C_(x)-C_(y))cycloalkyl) are defined in an analogous manner as having from x to y carbon atoms and being either unsubstituted or substituted with one or more R^(S). Examples of unsubstituted (C₃-C₄₀)cycloalkyl are unsubstituted (C₃-C₂₀)cycloalkyl, unsubstituted (C₃-C₁₀)cycloalkyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, and cyclodecyl. Examples of substituted (C₃-C₄₀)cycloalkyl are substituted (C₃-C₂₀)cycloalkyl, substituted (C₃-C₁₀)cycloalkyl, cyclopentanon-2-yl, and 1-fluorocyclohexyl.

Examples of (C₁-C₄₀)hydrocarbylene include unsubstituted or substituted (C₆-C₄₀)arylene, (C₃-C₄₀)cycloalkylene, and (C₁-C₄₀)alkylene (e.g., (C₁-C₂₀)alkylene). In some embodiments, the diradicals are on the same carbon atom (e.g., CH₂) or on adjacent carbon atoms (i.e., 1,2-diradicals), or are spaced apart by one, two, or more than two intervening carbon atoms (e.g., respective 1,3-diradicals, 1,4-diradicals, etc.). Some diradicals include α,ω-diradical. The α,ω-diradical is a diradical that has maximum carbon backbone spacing between the radical carbons. Some examples of (C₂-C₂₀)alkylene α,ω-diradicals include ethan-1,2-diyl (i.e. CH₂CH₂), propan-1,3-diyl (i.e. CH₂CH₂CH₂), 2-methylpropan-1,3-diyl (i.e. CH₂CH(CH₃)CH₂). Some examples of (C₆-C₄₀)arylene α,ω-diradicals include phenyl-1,4-diyl, napthalen-2,6-diyl, or napthalen-3,7-diyl.

The term “(C₁-C₄₀)alkylene” means a saturated straight chain or branched chain diradical (i.e., the radicals are not on ring atoms) of from 1 to 40 carbon atoms that is unsubstituted or substituted by one or more R^(S). Examples of unsubstituted (C₁-C₄₀)alkylene are unsubstituted (C₁-C₂₀)alkylene, including unsubstituted—CH₂CH₂—, —(CH₂)₃—, —(CH₂)₄—, —(CH₂)₅—, —(CH₂)₆—, —(CH₂)₇—, —(CH₂)₈—, —CH₂C*HCH₃, and —(CH₂)₄C*(H)(CH₃), in which “C*” denotes a carbon atom from which a hydrogen atom is removed to form a secondary or tertiary alkyl radical. Examples of substituted (C₁-C₄₀)alkylene are substituted (C₁-C₂₀)alkylene, —CF₂—, —C(O)—, and —(CH₂)₁₄C(CH₃)₂(CH₂)₅— (i.e., a 6,6-dimethyl substituted normal-1,20-eicosylene). Since as mentioned previously two R^(S) may be taken together to form a (C₁-C₁₈)alkylene, examples of substituted (C₁-C₄₀)alkylene also include 1,2-bis(methylene)cyclopentane, 1,2-bis(methylene)cyclohexane, 2,3-bis(methylene)-7,7-dimethyl-bicyclo[2.2.1]heptane, and 2,3-bis(methylene)bicyclo [2.2.2] octane.

The term “(C₃-C₄₀)cycloalkylene” means a cyclic diradical (i.e., the radicals are on ring atoms) of from 3 to 40 carbon atoms that is unsubstituted or substituted by one or more R^(S).

The term “heteroatom,” refers to an atom other than hydrogen or carbon. Examples of groups containing one or more than one heteroatom include 0, S, S(O), S(O)₂, Si(R^(C))₂, P(R^(P)), N(R^(N)), —N═C(R^(C))₂, —Ge(R^(C))₂—, or —Si(R^(C))—, where each R^(C) and each R^(P) is unsubstituted (C₁-C₁₈)hydrocarbyl or —H, and where each R^(N) is unsubstituted (C₁-C₁₈)hydrocarbyl. The term “heterohydrocarbon” refers to a molecule or molecular framework in which one or more carbon atoms are replaced with a heteroatom. The term “(C₁-C₄₀)heterohydrocarbyl” means a heterohydrocarbon radical of from 1 to 40 carbon atoms, and the term “(C₁-C₄₀)heterohydrocarbylene” means a heterohydrocarbon diradical of from 1 to 40 carbon atoms, and each heterohydrocarbon has one or more heteroatoms. The radical of the heterohydrocarbyl is on a carbon atom or a heteroatom, and diradicals of the heterohydrocarbyl may be on: (1) one or two carbon atom, (2) one or two heteroatoms, or (3) a carbon atom and a heteroatom. Each (C₁-C₄₀)heterohydrocarbyl and (C₁-C₄₀)heterohydrocarbylene may be unsubstituted or substituted (by one or more R^(S)), aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (including mono- and poly-cyclic, fused and non-fused polycyclic), or acyclic.

The (C₁-C₄₀)heterohydrocarbyl may be unsubstituted or substituted. Non-limiting examples of the (C₁-C₄₀)heterohydrocarbyl include (C₁-C₄₀)hetero alkyl, (C₁-C₄₀)hydrocarbyl-O—, (C₁-C₄₀)hydrocarbyl-S—, (C₁-C₄₀)hydrocarbyl-S(O)—, (C₁-C₄₀)hydrocarbyl-S(O)₂—, (C₁-C₄₀)hydrocarbyl-Si(R^(C))₂—, (C₁-C₄₀)hydrocarbyl-N(R^(N))—, (C₁-C₄₀)hydrocarbyl-P(R^(P))—, (C₂-C₄₀)heterocycloalkyl, (C₂-C₁₉)heterocycloalkyl-(C₁-C₂₀)alkylene, (C₃-C₂₀)cycloalkyl-(C₁-C₁₉)heteroalkylene, (C₂-C₁₉)heterocycloalkyl-(C₁-C₂₀)heteroalkylene, (C₁-C₅₀)heteroaryl, (C₁-C₁₉)heteroaryl-(C₁-C₂₀)alkylene, (C₆-C₂₀)aryl-(C₁-C₁₉)heteroalkylene, or (C₁-C₁₉)heteroaryl-(C₁-C₂₀)heteroalkylene.

The term “(C₁-C₄₀)heteroaryl” means an unsubstituted or substituted (by one or more R^(S)) mono-, bi- or tricyclic heteroaromatic hydrocarbon radical of from 4 to 40 total carbon atoms and from 1 to 10 heteroatoms, and the mono-, bi- or tricyclic radical comprises 1, 2 or 3 rings, respectively, wherein the 2 or 3 rings independently are fused or non-fused and at least one of the 2 or 3 rings is heteroaromatic. Other heteroaryl groups (e.g., (C_(x)C_(y))heteroaryl generally, such as (C₁-C₁₂)heteroaryl) are defined in an analogous manner as having from x to y carbon atoms (such as 1 to 12 carbon atoms) and being unsubstituted or substituted by one or more than one R^(S). The monocyclic heteroaromatic hydrocarbon radical is a 5-membered or 6-membered ring. The 5-membered ring has 5 minus h carbon atoms, wherein h is the number of heteroatoms and may be 1, 2, or 3; and each heteroatom may be O, S, N, or P. Examples of 5-membered ring heteroaromatic hydrocarbon radical are pyrrol-1-yl; pyrrol-2-yl; furan-3-yl; thiophen-2-yl; pyrazol-1-yl; is oxazol-2-yl; isothiazol-5-yl; imidazol-2-yl; oxazol-4-yl; thiazol-2-yl; 1,2,4-triazol-1-yl; 1,3,4-oxadiazol-2-yl; 1,3,4-thiadiazol-2-yl; tetrazol-1-yl; tetrazol-2-yl; and tetrazol-5-yl. The 6-membered ring has 6 minus h carbon atoms, wherein h is the number of heteroatoms and may be 1 or 2 and the heteroatoms may be N or P. Examples of 6-membered ring heteroaromatic hydrocarbon radical are pyridine-2-yl; pyrimidin-2-yl; and pyrazin-2-yl. The bicyclic heteroaromatic hydrocarbon radical can be a fused 5,6- or 6,6-ring system. Examples of the fused 5,6-ring system bicyclic heteroaromatic hydrocarbon radical are indol-1-yl; and benzimidazole-1-yl. Examples of the fused 6,6-ring system bicyclic heteroaromatic hydrocarbon radical are quinolin-2-yl; and isoquinolin-1-yl. The tricyclic heteroaromatic hydrocarbon radical can be a fused 5,6,5-; 5,6,6-; 6,5,6-; or 6,6,6-ring system. An example of the fused 5,6,5-ring system is 1,7-dihydropyrrolo[3,2-f]indol-1-yl. An example of the fused 5,6,6-ring system is 1H-benzo[f]indol-1-yl. An example of the fused 6,5,6-ring system is 9H-carbazol-9-yl. An example of the fused 6,6,6-ring system is acrydin-9-yl.

The aforementioned heteroalkyl may be saturated straight or branched chain radicals containing (C₁-C₄₀) carbon atoms, or fewer carbon atoms and one or more of the heteroatoms. Likewise, the heteroalkylene may be saturated straight or branched chain diradicals containing from 1 to 50 carbon atoms and one or more than one heteroatoms. The heteroatoms, as defined above, may include Si(R^(C))₃, Ge(R^(C))₃, Si(R^(C))₂, Ge(R^(C))₂, P(R^(P))₂, P(R^(P)), N(R^(N))₂, N(R^(N)), N, O, OR^(C), S, SR^(C), S(O), and S(O)₂, wherein each of the heteroalkyl and heteroalkylene groups are unsubstituted or substituted by one or more R^(S).

Examples of unsubstituted (C₂-C₄₀)heterocycloalkyl are unsubstituted (C₂-C₂₀)heterocycloalkyl, unsubstituted (C₂-C₁₀)heterocycloalkyl, aziridin-1-yl, oxetan-2-yl, tetrahydrofuran-3-yl, pyrrolidin-1-yl, tetrahydrothiophen-S,S-dioxide-2-yl, morpholin-4-yl, 1,4-dioxan-2-yl, hexahydroazepin-4-yl, 3-oxa-cyclooctyl, 5-thio-cyclononyl, and 2-aza-cyclodecyl.

The term “halogen atom” or “halogen” means the radical of a fluorine atom (F), chlorine atom (Cl), bromine atom (Br), or iodine atom (I). The term “halide” means anionic form of the halogen atom:fluoride (F⁻), chloride (Cl⁻), bromide (Br⁻), or iodide (I⁻).

The term “saturated” means lacking carbon-carbon double bonds, carbon-carbon triple bonds, and (in heteroatom-containing groups) carbon-nitrogen, carbon-phosphorous, and carbon-silicon double bonds. Where a saturated chemical group is substituted by one or more substituents R^(S), one or more double and/or triple bonds optionally may or may not be present in substituents R^(S). The term “unsaturated” means containing one or more carbon-carbon double bonds, carbon-carbon triple bonds, and (in heteroatom-containing groups) carbon-nitrogen, carbon-phosphorous, and carbon-silicon double bonds, not including any such double bonds that may be present in substituents R^(S), if any, or in (hetero) aromatic rings, if any.

In some embodiments the catalyst systems comprising a metal-ligand complex of Formula (I) may be rendered catalytically active by any technique known in the art for activating metal-based catalysts of olefin polymerization reactions. For example, comprising a metal ligand complex of Formula (I) may be rendered catalytically active by contacting the complex to, or combining the complex with, an activating cocatalyst. Suitable activating cocatalysts for use herein include alkyl aluminums; polymeric or oligomeric alumoxanes (also known as aluminoxanes); neutral Lewis acids; and non-polymeric, non-coordinating, ion-forming compounds (including the use of such compounds under oxidizing conditions). A suitable activating technique is bulk electrolysis. Combinations of one or more of the foregoing activating cocatalysts and techniques are also contemplated. The term “alkyl aluminum” means a monoalkyl aluminum dihydride or monoalkylaluminum dihalide, a dialkyl aluminum hydride or dialkyl aluminum halide, or a trialkylaluminum. Examples of polymeric or oligomeric alumoxanes include methylalumoxane, triisobutylaluminum-modified methylalumoxane, and isobutylalumoxane.

Lewis acid activators (cocatalysts) include Group 13 metal compounds containing from 1 to 3 (C₁-C₂₀)hydrocarbyl substituents as described herein. In one embodiment, Group 13 metal compounds are tri((C₁-C₂₀)hydrocarbyl)-substituted-aluminum or tri((C₁-C₂₀)hydrocarbyl)-boron compounds. In other embodiments, Group 13 metal compounds are tri(hydrocarbyl)-substituted-aluminum, tri(hydrocarbyl)-boron compounds, tri((C₁-C₁₀)alkyl)aluminum, tri((C₆-C₁₈)aryl)boron compounds, and halogenated (including perhalogenated) derivatives thereof. In further embodiments, Group 13 metal compounds are tris(fluoro-substituted phenyl)boranes, tris(pentafluorophenyl)borane. In some embodiments, the activating cocatalyst is a tetrakis((C₁-C₂₀)hydrocarbyl borate (e.g. trityl tetrafluoroborate) or a tri((C₁-C₂₀)hydrocarbyl)ammonium tetra((C₁-C₂₀)hydrocarbyl)borane (e.g. bis(octadecyl)methylammonium tetrakis(pentafluorophenyl)borane). As used herein, the term “ammonium” means a nitrogen cation that is a ((C₁-C₂₀)hydrocarbyl)₄N⁺ a ((C₁-C₂₀)hydrocarbyl)₃N(H)⁺, a ((C₁-C₂₀)hydrocarbyl)₂N(H)₂ ⁺, (C₁-C₂₀)hydrocarbyl)₂N(H)₃ ⁺, or N(H)₄ ⁺, wherein each (C₁-C₂₀)hydrocarbyl, when two or more are present, may be the same or different.

Combinations of neutral Lewis acid activators (cocatalysts) include mixtures comprising a combination of a tri((C₁-C₄)alkyl)aluminum and a halogenated tri((C₆-C₁₈)aryl)boron compound, especially a tris(pentafluorophenyl)borane. Other embodiments are combinations of such neutral Lewis acid mixtures with a polymeric or oligomeric alumoxane, and combinations of a single neutral Lewis acid, especially tris(pentafluorophenyl)borane with a polymeric or oligomeric alumoxane. Ratios of numbers of moles of (metal-ligand complex): (tris(pentafluoro-phenylborane):(alumoxane) [e.g., (Group 4 metal-ligand complex):(tris(pentafluoro-phenylborane):(alumoxane)] are from 1:1:1 to 1:10:30, in other embodiments, from 1:1:1.5 to 1:5:10.

The catalyst system comprising the metal-ligand complex of Formula (I) may be activated to form an active catalyst composition by combination with one or more cocatalysts, for example, a cation forming cocatalyst, a strong Lewis acid, or combinations thereof. Suitable activating cocatalysts include polymeric or oligomeric aluminoxanes, especially methyl aluminoxane, as well as inert, compatible, noncoordinating, ion forming compounds. Exemplary suitable cocatalysts include, but are not limited to: modified methyl aluminoxane (MMAO), bis(hydrogenated tallow alkyl)methyl tetrakis(pentafluorophenyl)borate(1⁻) amine, and combinations thereof.

In some embodiments, one or more of the foregoing activating cocatalysts are used in combination with each other. An especially preferred combination is a mixture of a tri((C₁-C₄)hydrocarbyl)aluminum, tri((C₁-C₄)hydrocarbyl)borane, or an ammonium borate with an oligomeric or polymeric alumoxane compound. The ratio of total number of moles of one or more metal-ligand complexes of Formula (I) to total number of moles of one or more of the activating cocatalysts is from 1:10,000 to 100:1. In some embodiments, the ratio is at least 1:5000, in some other embodiments, at least 1:1000; and 10:1 or less, and in some other embodiments, 1:1 or less. When an alumoxane alone is used as the activating cocatalyst, preferably the number of moles of the alumoxane that are employed is at least 100 times the number of moles of the metal-ligand complex of Formula (I). When tris(pentafluorophenyl)borane alone is used as the activating cocatalyst, in some other embodiments, the number of moles of the tris(pentafluorophenyl)borane that are employed to the total number of moles of one or more metal-ligand complexes of Formula (I) from 0.5:1 to 10:1, from 1:1 to 6:1, or from 1:1 to 5:1. The remaining activating cocatalysts are generally employed in approximately mole quantities equal to the total mole quantities of one or more metal-ligand complexes of Formula (I).

The reactivity ratios are determined by the resulting difference in polymerization rates (i.e., selectivity) between ethylene and the C₃-C₁₂ α-olefin with the polymerization catalyst in the polymerization process. It is believed that steric interactions for the polymerization catalysts result in polymerization of ethylene more selectively than α-olefins such as C₃-C₁₂ α-olefins (i.e., the catalyst preferentially polymerizes ethylene in the presence of the α-olefin). Again without being bound by theory, it is believed that such steric interactions cause the catalyst, for example, the homogenous catalyst prepared with or from the metal-ligand complex of Formula (I) to adopt a conformation that allows ethylene to access the M substantially more easily, or adopt a reactive conformation more readily, or both than the catalyst allows the α-olefin to do so.

For random copolymers in which the identity of the last monomer inserted dictates the rate at which subsequent monomers insert, the terminal copolymerization model is employed. In this model insertion reactions of the type

$\begin{matrix} {{{\ldots \mspace{14mu} M_{i}C^{*}} + M_{j}}\overset{k_{ij}}{\rightarrow}{\ldots \mspace{14mu} M_{i}M_{j}C^{*}}} & \left( {{Equation}\mspace{14mu} 1} \right) \end{matrix}$

where C* represents the catalyst, M represents monomeri, and k_(ij) is the rate constant having the rate equation

R _(P) _(ij) =k _(ij)[ . . . M _(i) C*][M _(j)]  (Equation 2)

The comonomer mole fraction (i=2) in the reaction media is defined by the equation:

$\begin{matrix} {f_{2} = \frac{\left\lbrack M_{2} \right\rbrack}{\left\lbrack M_{1} \right\rbrack + \left\lbrack M_{2} \right\rbrack}} & \left( {{Equation}\mspace{14mu} 3} \right) \end{matrix}$

A simplified equation for comonomer composition can be derived as disclosed in George Odian, Principles of Polymerization, Second Edition, John Wiley and Sons, 1970, as follows:

$\begin{matrix} {F_{1} = {{1 - F_{2}} = \frac{{r_{1}\left( {1 - f_{2}} \right)}^{2} + {\left( {1 - f_{2}} \right)f_{2}}}{{r_{1}\left( {1 - f_{2}} \right)}^{2} + {2\left( {1 - f_{2}} \right)f_{2}} + {r_{2}f_{2}^{2}}}}} & \left( {{Equation}\mspace{14mu} 4} \right) \end{matrix}$

From this equation the mole fraction of comonomer in the polymer is solely dependent on the mole fraction of comonomer in the reaction media and two temperature dependent reactivity ratios defined in terms of the insertion rate constants as:

$\begin{matrix} {r_{1} = {{\frac{k_{11}}{k_{12}}\mspace{14mu} r_{2}} = \frac{k_{22}}{k_{21}}}} & \left( {{Equation}\mspace{14mu} 5} \right) \end{matrix}$

For this model as well the polymer composition is a function only of temperature dependent reactivity ratios and comonomer mole fraction in the reactor. The same is also true when reverse comonomer or monomer insertion may occur or in the case of the interpolymerization of more than two monomers.

Reactivity ratios for use in the foregoing models may be predicted using well known theoretical techniques or empirically derived from actual polymerization data. Suitable theoretical techniques are disclosed, for example, in B. G. Kyle, Chemical and Process Thermodynamics, Third Addition, Prentice-Hall, 1999 and in Redlich-Kwong-Soave (RKS) Equation of State, Chemical Engineering Science, 1972, pp 1197-1203. Commercially available software programs may be used to assist in deriving reactivity ratios from experimentally derived data. One example of such software is Aspen Plus from Aspen Technology, Inc., Ten Canal Park, Cambridge, Mass. 02141-2201 USA.

Test Methods

Melt Index (I₂) and (I₁₀)

Melt index (I₂) values for the multimodal ethylene-based polymers can be measured in accordance to ASTM D1238 at 190° C. at 2.16 kg. Similarly, melt index (I₁₀) values for the multimodal ethylene-based polymers can be measured in accordance to ASTM D1238 at 190° C. at 10 kg. The values are reported in g/10 min, which corresponds to grams eluted per 10 minutes. The melt index (I₂) values for the first ethylene-based component (MI₁), the second ethylene-based component (MI₂), and the third ethylene-based component (MI₃) can be calculated according to Equation 30 and the methodology described below.

Density

Density measurements for the multimodal ethylene-based polymers can be made in accordance with ASTM D792, Method B. For the first and second ethylene-based components, the density values can be obtained using Equation 28 and the methodology described below. For the third ethylene-based component, the density value can be calculated using Equation 29.

Conventional Gel Permeation Chromatography (Conventional GPC)

The chromatographic system consisted of a PolymerChar GPC-IR (Valencia, Spain) high temperature GPC chromatograph equipped with an internal IR5 infra-red detector (IR5). The autosampler oven compartment was set at 160° C. and the column compartment was set at 150° C. The columns used were 4 Agilent “Mixed A” 30 cm 20-micron linear mixed-bed. The chromatographic solvent used was 1,2,4 trichlorobenzene and contained 200 ppm of butylated hydroxytoluene (BHT). The solvent source was nitrogen sparged. The injection volume used was 200 microliters and the flow rate was 1.0 milliliters/minute.

Calibration of the GPC column set was performed with at least 20 narrow molecular weight distribution polystyrene standards with molecular weights ranging from 580 to 8,400,000 g/mol and were arranged in 6 “cocktail” mixtures with at least a decade of separation between individual molecular weights. The standards were purchased from Agilent Technologies. The polystyrene standards were prepared at 0.025 grams in 50 milliliters of solvent for molecular weights equal to or greater than 1,000,000 g/mol, and 0.05 grams in 50 milliliters of solvent for molecular weights less than 1,000,000 g/mol. The polystyrene standards were dissolved at 80° C. with gentle agitation for 30 minutes. The polystyrene standard peak molecular weights were converted to ethylene-based polymer molecular weights using Equation 6 (as described in Williams and Ward, J. Polym. Sci., Polym. Let., 6, 621 (1968)):

M _(polyethylene) =A×(M _(polystyrene))  (Equation 6)

where M is the molecular weight, A has a value of 0.4315 and B is equal to 1.0.

A fifth order polynomial was used to fit the respective ethylene-based polymer-equivalent calibration points. A small adjustment to A (from approximately 0.39 to 0.44) was made to correct for column resolution and band-broadening effects such that NIST standard NBS 1475 is obtained at a molecular weight of 52,000 g/mol.

The total plate count of the GPC column set was performed with Eicosane (prepared at 0.04 g in 50 milliliters of TCB and dissolved for 20 minutes with gentle agitation). The plate count (Equation 7) and symmetry (Equation 8) were measured on a 200 microliter injection according to the following equations:

$\begin{matrix} {{{Plate}\mspace{14mu} {Count}} = {5.54 \times \left( \frac{{RV}_{{Peak}\mspace{14mu} {Max}}}{{Peak}\mspace{14mu} {Width}\mspace{14mu} {at}\mspace{14mu} {half}\mspace{14mu} {height}} \right)^{2}}} & \left( {{Equation}\mspace{14mu} 7} \right) \end{matrix}$

where RV is the retention volume in milliliters, the peak width is in milliliters, the peak max is the maximum height of the peak, and half height is one half of the height of the peak maximum.

$\begin{matrix} {{Symmetry} = \frac{\left( {{{Rear}\mspace{14mu} {Peak}\mspace{14mu} {RV}_{{one}\mspace{14mu} {tenth}\mspace{14mu} {height}}} - {RV}_{{Peak}\mspace{14mu} \max}} \right)}{\left( {{RV}_{{Peak}\mspace{14mu} \max} - {{Front}\mspace{14mu} {Peak}\mspace{14mu} {RV}_{{one}\mspace{14mu} {tenth}\mspace{14mu} {height}}}} \right)}} & \left( {{Equation}\mspace{14mu} 8} \right) \end{matrix}$

where RV is the retention volume in milliliters and the peak width is in milliliters, Peak max is the maximum position of the peak, one tenth height is one tenth of the height of the peak maximum, and where rear peak refers to the peak tail at later retention volumes than the peak max and where front peak refers to the peak front at earlier retention volumes than the peak max. The plate count for the chromatographic system should be greater than 22,000 and symmetry should be between 0.98 and 1.22.

Samples were prepared in a semi-automatic manner with the PolymerChar “Instrument Control” Software, wherein the samples were weight-targeted at 2 mg/ml, and the solvent (contained 200 ppm BHT) was added to a pre nitrogen-sparged septa-capped vial, via the PolymerChar high temperature autosampler. The samples were dissolved for 3 hours at 160° C. under “low speed” shaking.

The calculations of M_(n(GPC)), M_(w(GPC)), and M_(z(GPC)) were based on GPC results using the internal IRS detector (measurement channel) of the PolymerChar GPC-IR chromatograph according to Equations 9-12, using PolymerChar GPCOne™ software, the baseline-subtracted IR chromatogram at each equally-spaced data collection point i (IR_(i)) and the ethylene-based polymer equivalent molecular weight obtained from the narrow standard calibration curve for the point i (M_(polyethylene,i) in g/mol) from Equation 6. Subsequently, a GPC molecular weight distribution (GPC-MWD) plot (wt_(GPC)(lgMW) vs. lgMW plot, where wt_(GPC)(lgMW) is the weight fraction of ethylene-based polymer molecules with a molecular weight of lgMW) for the ethylene-based polymer sample can be obtained. Molecular weight is in g/mol and wt_(GPC)(lgMW) follows the Equation 9.

∫wt _(GPC)(lg MW)d lg MW=1.00  (Equation 9)

Number-average molecular weight M_(n(GPC)), weight-average molecular weight M_(w(GPC)) and z-average molecular weight M_(z(GPC)) can be calculated as the following equations.

$\begin{matrix} {M_{n{({GPC})}} = \frac{\sum\limits^{i}{IR}_{i}}{\sum\limits^{i}\left( \frac{{IR}_{i}}{M_{polyethylene},_{i}} \right)}} & \left( {{Equation}\mspace{14mu} 10} \right) \\ {M_{w{({GPC})}} = \frac{\sum\limits^{i}\left( {{IR}_{i}*M_{{polyethylene},_{i}}} \right)}{\sum\limits^{i}{IR}_{i}}} & \left( {{Equation}\mspace{14mu} 11} \right) \\ {M_{z{({GPC})}} = \frac{\sum\limits^{i}\left( {{IR}_{i}*M_{{polyethylene},_{i}^{2}}} \right)}{\sum\limits^{i}\left( {{IR}_{i}*M_{{polyethylene},_{i}}} \right)}} & \left( {{Equation}\mspace{14mu} 12} \right) \end{matrix}$

In order to monitor the deviations over time, a flow rate marker (decane) was introduced into each sample via a micropump controlled with the PolymerChar GPC-IR system. This flow rate marker (FM) was used to linearly correct the pump flow rate (Flowrate(nominal)) for each sample by RV alignment of the respective decane peak within the sample (RV(FM Sample)) to that of the decane peak within the narrow standards calibration (RV(FM Calibrated)). Any changes in the time of the decane marker peak are then assumed to be related to a linear-shift in flow rate (Flowrate(effective)) for the entire run. To facilitate the highest accuracy of a RV measurement of the flow marker peak, a least-squares fitting routine is used to fit the peak of the flow marker concentration chromatogram to a quadratic equation. The first derivative of the quadratic equation is then used to solve for the true peak position. After calibrating the system based on a flow marker peak, the effective flow rate (with respect to the narrow standards calibration) is calculated as Equation 13. Processing of the flow marker peak was done via the PolymerChar GPCOne™ Software. Acceptable flow rate correction is such that the effective flowrate should be within 0.5% of the nominal flowrate.

Flow rate_(effective)=Flow rate_(nominal)×(RV(FM _(calibrated))/RV(FM _(sample)))  (Equation 13)

IR5 GPC Comonomer Content (GPC-CC) Plot

A calibration for the IRS detector ratioing was performed using at least ten ethylene-based polymer standards (ethylene-based polymer homopolymer and ethylene/octene copolymers) of known short chain branching (SCB) frequency (The comonomer content of the reference materials is determined using 13C NMR analysis in accordance with techniques described, for example, in U.S. Pat. No. 5,292,845 (Kawasaki, et al.) and by J. C. Randall in Rev. Macromol. Chem. Phys., C29, 201-317a, which are incorporated herein by reference), ranging from homopolymer (0 SCB/1000 total C) to approximately 50 SCB/1000 total C, where total C is equal to the carbons in backbone plus the carbons in branches. Each standard had a weight-average molecular weight from 36,000 g/mole to 126,000 g/mole and had a molecular weight distribution from 2.0 to 2.5, as determined by GPC. Typical Copolymer Standards properties and measurements are shown in Table A.

TABLE A “Copolymer” Standards Wt % lR5 SCB/1000 M_(w(GPC)) M_(W(GPC))/ Comonomer Area ratio Total C g/mol M_(n(GPC)) 0.0 0.1809 0.0 38,400 2.20 1.1 0.1810 1.4 107,000 2.09 5.4 0.1959 6.8 37,400 2.16 8.6 0.2043 10.8 36,800 2.20 9.4 0.2031 11.8 103,200 2.26 14.0 0.2152 17.5 36,000 2.19 14.3 0.2161 17.9 103,600 2.20 23.1 0.2411 28.9 37,300 2.22 35.9 0.2708 44.9 42,200 2.18 39.2 0.2770 49.0 125,600 2.22

The “IR5 Area Ratio (or “IR5_(Methyl Channel Area)/IR5_(Measurement Channel Area)”)” of “the baseline-subtracted area response of the IR5 methyl channel sensor” to “the baseline-subtracted area response of IR5 measurement channel sensor” (standard filters and filter wheel as supplied by PolymerChar: Part Number IR5_FWM01 included as part of the GPC-IR instrument) was calculated for each of the “Copolymer” standards. A linear fit of the Wt % Comonomer versus the “IR5 Area Ratio” was constructed in the form of the following Equation 14:

wt % Comonomer=A ₀+[A ₁(IR5_(Methyl Channel Area) /IR5_(Measurement Channel Area))]  (Equation 14)

Therefore, a GPC-CC (GPC-Comonomer Content) plot (wt % comonomer vs. lgMW) can be obtained. End-Group Correction of the wt % Comonomer data can be made via knowledge of the termination mechanism if there is significant spectral overlap with the comonomer termination (methyls) via the molecular weight determined at each chromatographic slice.

Crystallization Elution Fractionation (CEF)

Comonomer distribution analysis, also commonly called short chain branching distribution (SCBD), is measured with Crystallization Elution Fractionation (CEF) (PolymerChar, Spain) (Monrabal et al, Macromol. Symp. 257, 71-79 (2007), which is incorporated herein by reference) equipped with an IR (IR-4 or IR-5) detector (PolymerChar, Spain) and 2-angle light scattering detector Model 2040 (Precision Detectors, currently Agilent Technologies). Distilled anhydrous ortho-dichlorobenzene (ODCB) with 600 ppm antioxidant butylated hydroxytoluene (BHT) was used as solvent. For the autosampler with the capability of N₂ purge, no BHT was added. A GPC guard column (20 microns, or 10 microns, 50×7.5 mm) (Agilent Technologies) is installed just before the IR detector in the detector oven. Sample preparation is done with an autosampler at 160° C. for 2 hours under shaking at 4 mg/ml (unless otherwise specified). The injection volume is 300 The temperature profile of CEF is: crystallization at 3° C./min from 110° C. to 30° C., the thermal equilibrium at 30° C. for 5 minutes, elution at 3° C./min from 30° C. to 140° C. The flow rate during crystallization was at 0.052 ml/min. The flow rate during elution is at 0.50 ml/min. The data was collected at one data point/second.

The CEF column is packed by The Dow Chemical Company with glass beads at 125±6% (MO-SCI Specialty Products) with ⅛-inch stainless tubing. Glass beads are acid washed by MO-SCI Specialty by request from The Dow Chemical Company. Column volume is 2.06 ml. Column temperature calibration was performed by using a mixture of NIST Standard Reference Material Linear ethylene-based polymer 1475a (1.0 mg/ml) and Eicosane (2 mg/ml) in ODCB. Temperature was calibrated by adjusting elution heating rate so that NIST linear ethylene-based polymer 1475a has a peak temperature at 101.0° C., and Eicosane has a peak temperature of 30.0° C. The CEF column resolution was calculated with a mixture of NIST linear ethylene-based polymer 1475a (1.0 mg/ml) and hexacontane (Fluka, purum ≥97.0%, 1 mg/ml). A baseline separation of hexacontane and NIST ethylene-based polymer 1475a was achieved. The area of hexacontane (from 35.0 to 67.0° C.) to the area of NIST 1475a from 67.0 to 110.0° C. is 50 to 50, the amount of soluble fraction below 35.0° C. is less than 1.8 wt %. The CEF column resolution is defined in Equation 15:

$\begin{matrix} {{Resolution} = {\frac{{{Peak}\mspace{14mu} {Temperature}_{{NIST}\mspace{14mu} 1475A}} - {{Peak}\mspace{14mu} {Temperature}_{Hexacontane}}}{{{Width}\mspace{14mu} {at}\mspace{14mu} {Half}\mspace{14mu} {Height}_{{NIST}\mspace{14mu} 1475A}} + {{Width}\mspace{14mu} {at}\mspace{14mu} {Half}\mspace{14mu} {Height}_{Hexacontane}}} \geq 6.0}} & \left( {{Equation}\mspace{14mu} 15} \right) \end{matrix}$

where the half height width is measured in temperature and resolution is at least 6.0.

The CEF instrument was equipped with an Agilent (Santa Clara, Calif.) Model 2040 2-angle light scattering detector, and the light scattering was calibrated using the 90 degree signal channel with a known homopolymer ethylene-based polymer standard of known molecular weight (approximately 120,000 g/mol). The IR (infrared) detector was also calibrated for mass response. Molecular weight (M_(w(CEF))) at each elution point was calculated as a function of elution temperature in regions of adequate signal to noise. Area calculations (representing the total area of the 90 degree light scattering signal divided by the respective IR area and factored by the respective detector constants) was used to evaluate the weight-average molecular weight across regions of the elution temperature and to obtain a CEF-MW plot (M_(w(CEF)) vs. temperature curve). The area calculations have an inherent advantage of signal to noise over the continuous calculations. Both the IR and LS (light scattering) signals were subtracted from their baseline signal levels in accordance with normal chromatographic integration techniques.

A calculation of the “Critical Temperature (T_(critical)),” the weight fraction of polymer and the weight-average molecular weight in the temperature range of up to and including the critical temperature (M_(w(CEF)) of CEF fraction between 20° C. and T_(critical)) were obtained as follows:

Obtain a CEF-SCBD (CEF-short chain branching distribution) plot using weight fraction (wt_(CEF)(T)) at each temperature (T) from 20.0° C. to 119.9° C. with a temperature step increase of 0.2° C., where

∫_(20.0) ^(119.9) wt _(CEF)(T)dT=1.00  (Equation 16)

Critical temperature is defined by the density of the resin (in g/cc) according to

T _(critical)(° C.)=1108.1(° C.·cc/g)×density(g/cc)−952.1(° C.)  (Equation 17)

CEF weight fraction between 20° C. to T_(critical) is calculated from CEF-SCBD as

∫_(20.0) ^(T) ^(critical) wt _(CEF)(T)dT  (Equation 18)

Similarly, the weight-average molecular weight of the fraction from 20° C. up to and including the critical temperature (M_(w(CEF)) of CEF fraction between 20° C. and T_(critical)) was calculated as the area ratio of the sum of the 90 degree light scattering responses divided by the sum of the IR detector responses between 20° C. to T_(critical) and factored for the calibrated detector constants. The molecular weight calculations and calibrations were performed in GPCOne® software.

Numerical Deconvolution of Bivariate Data

Numerical Deconvolution of Bivariate Data is used to obtain the density, molecular weight, and melt index (I₂) of the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component. Numerical deconvolution of the combined CEF-SCBD (wt_(CEF)(T) vs. temperature (T) plot from CEF) and GPC-MWD (wt_(GPC)(lgMW)) vs. lgMW plot from conventional GPC) data was performed using Microsoft Excel® Solver (2013). For CEF-SCBD, the calculated weight fraction (wt_(sumCEF)(T)) versus temperature (T) data obtained using the method described in the CEF section (in the range of approximately 23 to 120° C.) was quelled to approximately 200 equally-spaced data points in order for a balance of appropriate iterative speed and temperature resolution. A single or series (up to 3 peaks for each component) of Exponentially-Modified Gaussian Distributions (Equation 19) were summed to represent each component (wt_(C,CEF)(T)), and the components were summed to yield the total weight (wt_(sum,CEF)(T)) at any temperature (T) as shown in Equations 20A-D.

$\begin{matrix} {y_{T,C,P} = {\frac{a_{0,C,P}}{2a_{3,C,P}} {e^{({\frac{a_{2,C,P}^{2}}{2a_{3,C,P}^{2}} + \frac{a_{1,C,P} - T}{a_{3,C,P}}})}\left\lbrack {\frac{1}{2} + {\frac{1}{2}{{erf}\left( {\frac{T - a_{1,C,P}}{\sqrt{2}a_{2,C,P}} - \frac{a_{2,C,P}}{\sqrt{2}a_{3,C,P}}} \right)}}} \right\rbrack}}} & \left( {{Equation}\mspace{14mu} 19} \right) \end{matrix}$

where C means component (C=1, 2 or 3), P means peak (P=1, 2, or 3), a_(0,C,P) is the chromatographic area in ° C. for the P-th peak of the C-th component, a_(1,C,P) is the peak center in ° C. for the P-th peak of the C-th component, a_(2,C,P) is the peak width in ° C. for the P-th peak of the C-th component, a_(3,C,P) is the peak tailing in ° C. for the P-th peak of the C-th component, and T is the elution temperature in ° C. In the case of a single Exponentially-Modified Gaussian Distributions is used to represent the CEF-SCBD of a component, y_(T,C,2)=Y_(T,C,3)=0. In the case of two Exponentially-Modified Gaussian Distributions are used to represent the CEF-SCBD of a component, only y_(T,C,3)=0.

wt _(C1,CEF)(T)=Σ_(p=1) ³ y _(T,1,P)  (Equation 20A)

wt _(C2,CEF)(T)=Σ_(p=1) ³ y _(T,2,P)  (Equation 20B)

wt _(C3,CEF)(T)=Σ_(p=1) ³ y _(T,3,P)  (Equation 20C)

wt _(sum,CEF)(T)=wt _(C1,CEF)(T)+wt _(C2,CEF)(T)+wt _(C3,CEF)(T)  (Equation 20D)

Weight fraction of each component (wk_(cEF)) from CEF-SCBD deconvolution can be expressed by

wf _(C1,CEF) =∫wt _(C1)(T)dT  (Equation 21A)

wf _(C2,CEF) =∫wt _(C2)(T)dT  (Equation 21B)

wf _(C3,CEF) =∫wt _(C3)(T)dT  (Equation 21C)

wt _(sum,CEF)(T)dT=1.00  (Equation 21D)

where wf_(C1,CEF) is the weight fraction of the first ethylene-based component obtained from CEF-SCBD deconvolution, wf_(C2,CEF) is the weight fraction of the second ethylene-based component obtained from CEF-SCBD deconvolution, wf_(C3,CEF) is the weight fraction of the third ethylene-based component obtained from CEF-SCBD deconvolution, and the sum of the fractions is normalized to 1.00.

For GPC-MWD, the MWD obtained by the Conventional GPC description section was imported into the same spreadsheet in 0.01 lg(MW/(g/mol)) increments between 2.00 and 7.00 (501 data points total). A Flory-Schulz Distribution with a weight-average molecular weight of M_(w,Target) and a polydispersity (M_(w)/M_(n)) of 2.0 is shown in the following equations.

$\begin{matrix} {\mspace{79mu} {{wt}_{{F - S},i} = {\left( \frac{3.03485 \times M_{i}}{M_{w,{Target}}} \right)^{2} \times e^{(\frac{{- 2}M_{i}}{M_{w,{Target}}})}}}} & \left( {{Equation}\mspace{14mu} 22} \right) \\ {\left. {\left. {\sum_{i = 0}^{499}{{wt}_{{F - S},i} \times {\lg \left( {M_{i + 1}\text{/}g\text{/}{mol}} \right)}}} \right) - {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)}} \right) = 1.00} & \left( {{Equation}\mspace{14mu} 23} \right) \\ {\mspace{79mu} {{{\lg \left( {M_{i + 1}\text{/}\left( {g\text{/}{mol}} \right)} \right)} - {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)}} = 0.01}} & \left( {{Equation}\mspace{14mu} 24} \right) \end{matrix}$

where wt_(F-S,i) is the weigh fraction of the molecules at lg(M_(i)/(g/mol)) (M_(i) in g/mol), i is integers ranging from 0 to 500 to represent each data point on the GPC-MWD plot and corresponding lg(M_(i)/(g/mol)) is 2+0.01×i.

The Flory-Schulz Distribution is subsequently broadened using a sum of a series normal distribution at each lg(M_(i)/(g/mol)). The weight fraction of the Normal Distribution with its peak value at lg(M_(i)/(g/mol)) is kept the same as the original Flory-Schulz Distribution. The broadened Flory-Schulz Distribution curve can be described as the following equation.

$\begin{matrix} {\left. {{wt}_{GPC}\left( {\lg \left( {M_{i}\text{/}g\text{/}{mol}} \right)} \right)} \right) = {\sum_{j = 0}^{500}{\frac{{wt}_{{F - S},j}}{\sqrt{2\; \pi}\sigma}e^{- \frac{{({{\lg {({M_{i}\text{/}{({g\text{/}{mol}})}})}} - {({2 + {0.01 \times j}})}})}^{2}}{2\; \sigma^{2}}}}}} & \left( {{Equation}\mspace{14mu} 25} \right) \end{matrix}$

where wt_(GPC)(lg(M_(i)/(g/mol))) is the weight fraction of the molecules at lg(M_(i)/(g/mol)), j is integers ranging from 0 to 500, σ is the standard deviation of the Normal Distribution. Therefore, molecular weight distribution curves for all three components can be expressed as the following equations. Number-average molecular weight (M_(n(GPC))), weight-average molecular weight (M_(w(GPC))), and MWD (M_(w(GPC))/M_(n(GPC))) can be calculated from the broadened Flory-Schulz Distribution.

$\begin{matrix} {{{wt}_{{C\; 1},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} = {{wf}_{{C\; 1},{GPC}} \times {\sum_{j = 0}^{500}{\frac{{wt}_{{F - S},{C\; 1},j}}{\sqrt{2\; \pi}\sigma_{C\; 1}}e^{- \frac{{({{\lg {({M_{i}\text{/}{({g\text{/}{mol}})}})}} - {({2 + {0.01 \times j}})}})}^{2}}{2\; \sigma_{C\; 1}^{2}}}}}}} & \left( {{Equation}\mspace{14mu} 26A} \right) \\ {{{wt}_{{C\; 2},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} = {{wf}_{{C\; 2},{GPC}} \times {\sum_{j = 0}^{500}{\frac{{wt}_{{F - S},{C\; 2},j}}{\sqrt{2\; \pi}\sigma_{C\; 2}}e^{- \frac{{({{\lg {({M_{i}\text{/}{({g\text{/}{mol}})}})}} - {({2 + {0.01 \times j}})}})}^{2}}{2\; \sigma_{C\; 2}^{2}}}}}}} & \left( {{Equation}\mspace{14mu} 26B} \right) \\ {{{wt}_{{C\; 3},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} = {{wf}_{{C\; 3},{GPC}} \times {\sum_{j = 0}^{500}{\frac{{wt}_{{F - S},{C\; 3},j}}{\sqrt{2\; \pi}\sigma_{C\; 3}}e^{- \frac{{({{\lg {({M_{i}\text{/}{({g\text{/}{mol}})}})}} - {({2 + {0.01 \times j}})}})}^{2}}{2\; \sigma_{C\; 3}^{2}}}}}}} & \left( {{Equation}\mspace{14mu} 26C} \right) \\ {{{wt}_{{sum},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} = {{{wt}_{{C\; 1},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} + {{wt}_{{C\; 2},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)} + {{wt}_{{C\; 3},{GPC}}\left( {\lg \left( {M_{i}\text{/}\left( {g\text{/}{mol}} \right)} \right)} \right)}}} & \left( {{Equation}\mspace{14mu} 26D} \right) \end{matrix}$

where σ is the normal distribution width parameter, the subscripts C1, C2 and C3 represent the first, the second and the third ethylene-based components, respectively. wf_(C1,GPC), Wf_(C2,GPC) and Wf_(C3,GPC) are the weight fractions of the first, the second and the third ethylene-based components from GPC-MWD, respectively.

Each of the paired components (the first ethylene-based component (C1), the second ethylene-based component (C2), and third ethylene-based component (C3)) from CEF-SCBD and GPC-MWD are considered equivalent masses for their respective techniques as shown in Equations 27A-E.

wf _(C1,CEF) +wf _(C2,CEF) +wf _(C3,CEF)=1.00  (Equation 27A)

Wf _(C1,CEF) +Wf _(C2,CEF) +Wf _(C3,CEF)=1.00  (Equation 27B)

wf _(C1,CEF) =wf _(C1,GPC)  (Equation 27C)

wf _(C2,CEF) =wf _(C2,GPC)  (Equation 27D)

wf _(C2,CEF) =wf _(C2,GPC)  (Equation 27E)

Process and catalyst data, including catalysts efficiency and reactor mass balance, can be leveraged for initial estimates of the relative weight production of each component. Alternatively, initial estimates of the weight fraction for each component can be compared by integrating partial areas of the CEF-SCBD or GPC-MWD plot of the multimodal ethylene-based polymer, especially noting visible areas with defined peaks or peak inflection points. For example, the peak area for each component in CEF-SCBD curve, if well-separated may be estimated by dropping vertical lines between peaks. Association of the molecular weight order and initial estimation of the molecular weight may be obtained from the peak positions of the associated component areas in the CEF-SCBD and CEF-MW plots and agreement should be expected with the GPC-CC measurements. In some cases, initial assignment of peak areas and composition may be obtained from a multi-modal GPC-MWD as the starting point and validated under the CEF-SCBD and CEF-MW plots.

Initial estimates of the peak width and tailing in CEF-SCBD for each component can be obtained from a calibration of peak width vs. temperature using a series of standard single-site samples such as those previously presented in Table A.

Microsoft Excel® Solver is programmed to minimize the combined sum of squares of residuals between the wt_(sum,GPC)(lgM_(i)) and the measured GPC-MWD, and sum of squares of residuals between the wt_(sum,CEF)(T) and the measured CEF-SCBD (wherein the sampling width and areas of the two observed distributions are normalized in regards to each other). There is equal weighting given to the GPC-MWD and CEF-SCBD fit as they are simultaneously converged. Initial estimated values for weight fraction and peak width in CEF-SCBD as well as molecular weight target for each component are used for the Microsoft Excel® Solver to begin with as described herein.

Co-crystallization effects which distort peak shape in CEF are compensated for by the use of the Exponentially-Modified Gaussian (EMG) peak fit and in extreme cases, the use of multiple (up to 3) EMG peaks summed to describe a single component. A component produced via a single site catalyst may be modeled by a single EMG peak. A component produced via a Ziegler-Natta catalyst may be modeled by 1, 2, or 3 EMG peaks, or a single EMG peak possessing a long low temperature-facing tail sufficing for a Ziegler-Natta component of very high density, very low molecular weight targets on the CEF-SCBD plot. In all cases, only a single broadened Flory-Schulz distribution (Equation 26A-C) is used with the weight fraction assigned as the associated sum of one or more of the EMG components from the CEF-SCBD model (Equations 27A-E).

The GPC deconvolution is constrained with a normal distribution width parameter (σ_(C1) or σ_(C2)) from Equation 26A, 26B between 0.000 and 0.170 (corresponding polydispersities of approximately 2.00 to 2.33) for the first and second ethylene-based components which are made via single site catalysts. The M_(w,Target) in Equation 22 is constrained to be lowest for the third ethylene-ethylene based component in these cases, since it is targeted to be the lowest from this specific reaction scheme. Note that it is not constrained by definition to be lowest in all possible cases, depending upon the desired performance target of the combined resin in-reactor blend. The ranking (preliminary estimation) of the two weight-average molecular weights (M_(w,Target)) of the first ethylene-based component and the second ethylene-based component is observed by the M_(w(CEF)) from the CEF-MW plot (M_(w(CEF)) vs. temperature curve) at the temperatures at which the first and second ethylene-based component peaks are observed on the CEF-SCBD plot (wt_(CEF)(T) vs. temperature curve). Therefore, the order of the molecular weights for the three components is well-known. A reactor mass balance yields the percentage mass (Wf) of Equation 26C of the third ethylene-based component, or alternatively it can be calculated from the deconvolution using Equation 26D, depending upon the strength of the known distribution models for CEF and GPC and the total weight fraction must sum to unity (Equations 27A-E).

In general, it has been found that approximately 20 solver iterations will typically reach good convergence on the solution using Excel®. If there is a disagreement in order of the peaks versus measured molecular weight by the CEF-MW plot and the observed comonomer wt % measurement measured via GPC-CC, then the data must be reconciled by changing the iteration starting points (temperature or lgMW) in Excel or changing the width and tail factors slightly such that the iteration will proceed with convergence to a consistent solution amongst the measurements, or the resolution of the measurements must be increased, or an additional peak may be added to the CEF-SCBD to better approximate the elution peak shape of the individual components. Such components could be modeled a-priori via several EMG distributions if they are prepared individually.

Additionally a predicted M_(w(CEF)) response for CEF-MW may be generated by using the weight-average molecular weight by GPC-MWD of each of the components multiplied by the observed weight fraction of each of the components at each point along the CEF-SCBD plot. The predicted M_(w(CEF)) needs to be in agreement with the measured M_(w(CEF)) in the CEF-MW plot. By plotting comonomer incorporation as a function of elution temperature based on a series of known copolymer standards, the GPC-CC plot can also be predicted using the measured M_(w(CEF)) and comonomer incorporation of individual component from CEF-MW and CEF-SCBD plots. The predicted GPC-CC plot needs to be in agreement with the measured GPC-CC.

A peak temperature vs. density correlation for the CEF-SCBD data is obtained using a series of linear ethylene-based polymer standard resins polymerized from single site catalysts of approximately 1 g/10 min melt index (I₂), or nominal weight-average molecular weight of approximately 105,000 g/mol by GPC, and polydispersities (or MWD) of less than 2.3 by GPC. At least 10 standard resins of known comonomer content, density, and molecular weight within the density range of 0.87 to 0.96 g/cc are used. Peak temperature and density data are fit with a 5th order polynomial curve to obtain the calibration curve.

A peak width and peak tail vs. peak temperature correlation is obtained similarly by fitting the peak width and peak tail vs. temperature of the above resins with a linear line, which is very useful for initial estimates in the deconvolution process.

The first ethylene-based component and the second ethylene-based component were noted in the resins presented herein directly from the CEF-SCBD deconvolution plot as the first two peaks between 35° C. and 90° C. elution temperature. A “Raw Density” (Density_(Raw)) was calculated from these observed peak positions using the calibration curve of peak temperature vs. density. The Density_(Raw) (in g/cc) was corrected to Density_(True) (in g/cc) accounting for molecular weight (in g/mol) contributions by using the Equation 28:

Density_(True)=Density_(Raw)−0.254g/cc×[lg(M _(w(GPC))/(g/mol))−5.02]  (Equation 28)

where M_(w(GPC)) is the weight-average molecular weight of the single component deconvoluted from GPC-MWD.

The density of the third ethylene-based component may be calculated based on the known density of the resin, Density_(True) of the first ethylene-based component, Density_(True) of the second ethylene-based component, and the weight fractions of each components according to the following Equation 29.

$\begin{matrix} {\frac{1}{{Density}_{measured}} = {\frac{{weight}\mspace{14mu} {fraction}\mspace{14mu} {of}\mspace{14mu} 1{st}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}}{{Density}_{True}\mspace{14mu} {of}\mspace{14mu} 1{st}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}} + \frac{{weight}\mspace{14mu} {fraction}\mspace{14mu} {of}\mspace{14mu} 2{nd}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}}{{Density}_{True}\mspace{14mu} {of}\mspace{14mu} 2{nd}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}} + \frac{{weight}\mspace{14mu} {fraction}\mspace{14mu} {of}\mspace{14mu} 3{rd}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}}{{density}\mspace{14mu} {of}\mspace{14mu} 3{rd}\mspace{14mu} {ethylene}\mspace{14mu} {based}\mspace{14mu} {component}}}} & \left( {{Equation}\mspace{14mu} 29} \right) \end{matrix}$

The melt index (I₂) of each ethylene-based component may be estimated from their weight-average molecular weight by the following equation:

lg(I ₂/(g/10 min))=−3.759×lg(M _(w(GPC))/(g/mol))+18.9  (Equation 30)

where M_(w(GPC)) is the weight average molecular weight (in g/mol) of the single component deconvoluted from GPC-MWD curve and I₂ is the melt index in (g/10 min). Note that the amount of long chain branching may change the coefficients.

Moreover, for the determination of product composition, direct sampling of a single reactor with a single catalyst with the same reactor conditions, a first reactor sampling for a series dual-reactor configuration, or sampling of both reactors for a parallel dual-reactor configuration may be used to aid in the determination of the density, melt index (I₂), GPC-MWD, and CEF-SCBD of each individual component of the multimodal ethylene-based polymer, especially providing that the reaction is effectively killed past the sampling point. This allows better confirmation in cases wherein the first and second ethylene-based component peak positions cannot adequately be determined from the 3-component mixture.

Direct examination and quantitation by analytical cross-fractionation in GPC-TREF, such as the PolymerChar CFC unit (Valencia, Spain) equipped with on-line light scattering and employing similar calibrations in bivariate space representing SCBD and molecular weight and calibrating the relationship to density may be used to measure amounts or discriminate more precisely of each of the components as well, especially for the initial estimates or in cases that may produce high co-crystallization or low resolution/discrimination of species particularly in both MWD and SCBD space. (Development of an Automated Cross-Fractionation Apparatus (TREF-GPC) for a Full Characterization of the Bivariate Distribution of Polyolefins. Polyolefin Characterization. Macromolecular Symposia, Volume 257, 2007, Pages 13-28. A. Oran, B. Monrabal, J. Sancho-Tello). Adequate resolution must be obtained in both lgMW and temperature space and verification should be done through both direct compositional ratioing, for example, IR-5 and light scattering molecular weight measurement. See Characterization of Chemical Composition along the Molar Mass Distribution in Polyolefin Copolymers by GPC Using a Modern Filter-Based IR Detector. Polyolefin Characterization—ICPC 2012 Macromolecular Symposia Volume 330, 2013, Pages 63-80, A. Oran, J. Montesinos, E. Lopez, P. del Hierro, B. Monrabal, J. R. Torres-Lapasio, M. C. Garcia-Alvarez-Coque. Deconvolution of the components must use a similar set of equations and analogous calibration verified by a series of single-site resins and resin blends.

EXAMPLES

The following examples illustrate features of the present disclosure but are not intended to limit the scope of the disclosure.

Comparative Examples 1 and 2

As described below, Comparative Examples 1 and 2 illustrate the synthesis of a trimodal polymer from a two reactor, three catalyst system. Specifically, the trimodal polymers produced through the two reactor, three catalyst system was produced in accordance with the process conditions provided in Table 1 as follows.

In the dual series reactor configuration, the effluent from the first polymerization reactor (containing solvent, monomer, comonomer, hydrogen, catalyst components, and dissolved polymer) exits the first reactor and is added to the second reactor separate from the other feeds to the second reactor. The dual series reactor system consisted of two liquid full, adiabatic, continuously stirred tank reactors (CSTRs).

Following catalyst deactivation and additive addition, the reactor effluent entered a devolatilization system where the polymer was removed from the non-polymer stream. The non-polymer stream was removed from the system. The isolated polymer melt was pelletized and collected.

All raw materials (monomer and comonomer) and the process solvent (a narrow boiling range high-purity paraffinic solvent, ISOPAR E) were purified with molecular sieves before introduction into the reaction environment. Hydrogen was supplied pressurized as a high purity grade and was not further purified. The reactor monomer feed stream was pressurized via a mechanical compressor to above reaction pressure. The solvent feed was pressurized via a pump to above reaction pressure. The comonomer feed was pressurized via a pump to above reaction pressure. The individual catalyst components were manually batch diluted to specified component concentrations with purified solvent and pressurized to above reaction pressure. All reaction feed flows were measured with mass flow meters and independently controlled with metering pumps.

Independent control of all fresh solvent, monomer, comonomer, hydrogen, and catalyst component feeds to each reactor was utilized. The total fresh feed streams to each reactor (solvent, monomer, comonomer, and hydrogen) were temperature controlled by passing the feed stream through a heat exchanger. The total fresh feed to each polymerization reactor was injected into the reactor in one or more locations. The catalyst components were injected into the polymerization reactor separate from the other feeds. An agitator in a CSTR reactor was responsible for continuous mixing of the reactants. Oil bath (for a CSTR reactor) provided fine tuning of the reactor temperature control.

For the reactor utilizing dual primary catalysts in one reactor, two calculated variables are controlled: (1) the total mass flow of primary catalyst 1 and primary catalyst 2, and (2) the mass fraction for primary catalyst 1 out of the total mass flow of both primary catalysts. The total mass flow of both primary catalysts was computer controlled to maintain the individual reactor monomer conversion at the specified target. The mass fraction of primary catalyst 1 was controlled to maintain the relative mass fraction of polymer produced by each catalyst in that individual reactor. The cocatalyst components for the reactor utilizing dual primary catalysts were fed based on calculated specified molar ratios to the total of both primary catalyst components.

TABLE 1 Comparative Comparative Example 1 Example 2 Reactor Configuration Type Dual Series Dual Series Comonomer type Type 1-octene 1-octene First Reactor Feed Solvent/Ethylene g/g 8.1 8.1 Mass Flow Ratio First Reactor Feed Comonomer/Ethylene g/g 0.57 0.59 Mass Flow Ratio First Reactor Feed Hydrogen/Ethylene g/g 2.91E-04 3.50E-04 Mass Flow Ratio First Reactor Temperature ° C. 150 150 First Reactor Pressure barg 28 28 First Reactor Ethylene Conversion % 77.1 77.0 First Reactor Catalyst 1 Type Type CAT-A CAT-A First Reactor Catalyst 2 Type Type CAT-B CAT-B First Reactor Catalyst 1 Active Metal Mass wt. % 76.9 76.9 Fraction (Hf/(Hf + Zr)) First Reactor Cocatalyst 1 Type Type CO-CAT-1 CO-CAT-1 First Reactor Cocatalyst 2 Type Type CO-CAT-2 CO-CAT-2 First Reactor, Molar ratio of Boron in Ratio 1.2 1.2 Cocatalyst 1 to Total metal in Catalysts 1 and 2 First Reactor, Molar ratio of Aluminum in Ratio 10 17 Cocatalyst 2 to Total Metal in Catalysts 1 and 2 Second Reactor Feed Solvent/Ethylene g/g 5.1 5.3 Mass Flow Ratio Second Reactor Feed Comonomer/ g/g 0.24 0.00 Ethylene Mass Flow Ratio Second Reactor Feed Hydrogen/Ethylene Mass Flow Ratio g/g 2.82E-03 2.82E-03 Second Reactor Temperature ° C. 210 210 Second Reactor Pressure barg 28 28 Second Reactor Ethylene Conversion % 81.4 81.9 Second Reactor Catalyst Type Type CAT-C CAT-C Second Reactor Cocatalyst Type Type CO-CAT-3 CO-CAT-3 Second Reactor Cocatalyst to Catalyst, Al mol/mol 4.6 4.6 to Ti molar ratio Melt index I₂ g/10 min 0.7 0.9 Melt index I₁₀ g/10 min 6.6 7.7 I₁₀/I₂ 9.4 8.6 Density g/cc 0.916 0.916

Formulas of Catalyst A and Catalyst B are shown below.

CATALYST C is a Ziegler-Natta catalyst. The heterogeneous Ziegler-Natta type catalyst-premix was prepared substantially according to U.S. Pat. No. 4,612,300, by sequentially adding to a volume of ISOPAR-E, a slurry of anhydrous magnesium chloride in ISOPAR-E, a solution of EtAlCl₂ in heptane, and a solution of Ti(O-iPr)₄ in heptane, to yield a composition containing a magnesium concentration of 0.20 M, and a ratio of Mg/Al/Ti of 40/12.5/3. An aliquot of this composition was further diluted with ISOPAR-E to yield a final concentration of 500 ppm Ti in the slurry. While being fed to, and prior to entry into, the polymerization reactor, the catalyst premix was contacted with a dilute solution of triethylaluminum (Et₃A1), in the molar Al to Ti ratio specified in Table 1, to give the active catalyst. The cocatalyst compositions are listed in Table 2 below.

TABLE 2 Description Chemical Name CO-CAT-A bis(hydrogenated tallow alkyl)methylammonium tetrakis(pentafluorophenyl)borate(1-) CO-CAT-B Aluminoxanes, iso-Bu Me, branched, cyclic and linear; modified methyl aluminoxane CO-CAT-C Et₃Al (Triethylaluminum)

Comparative Examples 1 and 2 illustrate that drift occurs in the trimodal polymer split for a two reactor, three catalyst system. Composition of Comparative Example 1 is tabulated in Table 3. A new batch of CAT-A and CAT-B were used to make Comparative Example 2. The catalyst flow was adjusted to achieve the same reactor exit ethylene concentration. However, higher “First Reactor Feed Hydrogen/Ethylene Mass Flow Ratio” was required for Comparative Example 2 than Comparative Example 1. At the same target catalyst ratio, the first ethylene-based component weight fraction increased from Comparative Example 1 to Comparative Example 2 as shown in FIG. 3, indicating that catalyst efficiency for CAT-A and CAT-B was impacted. The second ethylene-based component weight fraction decreased correspondingly from Comparative Example 1 to Comparative Example 2 as shown in FIG. 3. The peaks in FIG. 3 representing the first ethylene-based component and the second ethylene-based component varied between Comparative Example 1 and Comparative Example 2. This demonstrates that controlling the respective weight fractions (also called the split) of the first ethylene-based component and the second ethylene-based components in a two reactor, three catalyst system is more challenging.

TABLE 3 Composition of Comparative Example 1 Density (g/cc) 1 0.886 2 0.908 3 0.956 M_(w(GPC)) (g/mol) 1 196,133 2 114,601 3 21,068 M_(w(GPC))/M_(n(GPC)) 1 2.3 2 2.0 3 3.7 Melt Index, I₂(g/10 min) 1 0.10 2 0.76 3 442 Weight (Wt.) % 1 41 2 22 3 37 1 = first ethylene-based component 2 = second ethylene-based component 3 = third ethylene-based component *density of the third ethylene-based polymer component calculated based according to Equation 29

Without being bound to any particular theory, the weight fraction of each of the first, second and third components can be controlled more easily by a three reactor system, which can help the system achieve a desired split i.e., the desired amount of each ethylene-based component in the multimodal ethylene-based polymer.

Example 3

Example 3 provides a simulation of a polymer produced in three CSTRs in series, wherein the first CSTR reactor is adiabatic. The results of the simulation are provided in Table 4, below.

TABLE 4 Example 3 Reactor Configuration Type 3-CSTR in Series Comonomer type Type 1-octene First Reactor Feed Solvent/Ethylene Mass Flow Ratio g/g 7.0 First Reactor Feed Comonomer/Ethylene Mass Flow Ratio g/g 0.56 First Reactor Feed Hydrogen/Ethylene Mass Flow Ratio g/g 6.3E-05 First Reactor Temperature ° C. 185 First Reactor Pressure barg 50 First Reactor Ethylene Conversion % 86.0 First Reactor Catalyst 1 Type Type CAT-A First Reactor Cocatalyst 1 Type Type CO-CAT-1 First Reactor Cocatalyst 2 Type Type CO-CAT-2 First Reactor Component Polymer Weight Fraction wt. % 40.0 First Reactor Component Melt Index (I₂), MI₁ g/10 min 0.09 First Reactor Component Density g/cc 0.886 Second Reactor Feed Solvent/Ethylene Mass Flow Ratio g/g 3.0 Second Reactor Feed Comonomer/Ethylene Mass Flow Ratio g/g 0.05 Second Reactor Feed Hydrogen/Ethylene Mass Flow Ratio g/g 1.2E-05 Second Reactor Temperature ° C. 165 Second Reactor Pressure barg 50 Second Reactor Ethylene Conversion % 87.5 Second Reactor Catalyst 1 Type Type CAT-B Second Reactor Cocatalyst 1 Type Type CO-CAT-1 Second Reactor Cocatalyst 2 Type Type CO-CAT-2 Second Reactor Component Polymer Weight Fraction wt.% 20.5 Second Reactor Component Melt Index (I₂), MI₂ g/10 min 0.80 Second Reactor Component Density g/cc 0.908 Third Reactor Feed Solvent/Ethylene Mass Flow Ratio g/g 3.0 Third Reactor Feed Comonomer/Ethylene Mass Flow Ratio g/g 0.05 Third Reactor Feed Hydrogen/Ethylene Mass Flow Ratio g/g 3.0E-03 Third Reactor Temperature ° C. 200 Third Reactor Pressure barg 50 Third Reactor Ethylene Conversion % 70.0 Third Reactor Catalyst Type Type CAT-C Third Reactor Co-Catalystl Type Type CO-CAT-3 Third Reactor Component Polymer Weight Fraction wt. % 39.5 Third Reactor Component Melt Index (I₂), MI₃ g/10 min 293 Third Reactor Component Density g/cc 0.953 Overall Melt Index, I₂ g/10 min 0.70 Overall Density g/cc 0.916

The Composition of the trimodal polymer can be precisely controlled by the three reactor system. As shown in Table 4, density, melt index and weight fraction of the first, second and third ethylene-based components can be controlled by the “Solvent/Ethylene Mass Flow Ratio”, “Comonomer/Ethylene Mass Flow Ratio”, “Hydrogen/Ethylene Mass Flow Ratio”, “Reactor Temperature”, “Reactor Pressure” and “Ethylene Conversion” of each reactor, respectively. Unlike Comparative examples 1 and 2 discussed above, variation in catalyst efficiency (batch-to-batch) is not of concern, as one can separately control and adjust the catalyst feed to each reactor to reach the ethylene conversion targets in each reactor. The ethylene conversion and ethylene feed in each reactor determine the weight fraction of the first, second, and the third ethylene-based components.

It should be apparent to those skilled in the art that various modifications can be made to the described embodiments without departing from the spirit and scope of the claimed subject matter. Thus, it is intended that the specification cover modifications and variations of the described embodiments provided such modification and variations come within the scope of the appended claims and their equivalents. 

1. A method of producing a trimodal polymer in a solution polymerization process comprising: introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂α-olefin comonomer, solvent, and optionally hydrogen to a first solution polymerization reactor to produce an effluent comprising a first ethylene-based component, wherein the first ethylene-based component has a density (ρ₁) of 0.870 to 0.910 g/cc, and a weight-average molecular weight (M_(w(GPC),1)) of 150 to 350 kg/mol as measured according to Gel Permeation Chromatography (GPC); introducing the first ethylene-based component, at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a second solution polymerization reactor downstream from the first solution polymerization reactor to produce an effluent comprising the first ethylene-based component and a second ethylene-based component, wherein the second ethylene-based component has a density (ρ₂) from 0.895 to 0.925 g/cc, and a weight-average molecular weight (M_(w(GPC),2)) from 120 to 170 kg/mol; and introducing the first ethylene-based component, the second ethylene-based component, at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a third solution polymerization reactor downstream from the second solution polymerization reactor to produce an effluent comprising the trimodal polymer, wherein the trimodal polymer comprises the first ethylene-based component, the second ethylene-based component, and a third ethylene-based component, wherein the third ethylene-based component has a density (ρ₃) of 0.920 to 0.980 g/cc, and a weight-average molecular weight (M_(w(GPC),3)) of 18 to 60 kg/mol; wherein the first solution polymerization reactor or the third polymerization reactor is an adiabatic reactor; wherein different catalysts are used in the first solution polymerization reactor, the second polymerization reactor, and the third solution polymerization reactor; and wherein ρ₃>ρ₂>ρ₁, and M_(w(GPC),1)>M_(w(GPC),2)>M_(w(GPC),3).
 2. (canceled)
 3. The method of claim 1, wherein the first ethylene-based component has a melt index (MI₁) measured according to ASTM D1238 at 190° C. and 2.16 kg load, the second ethylene-based component has a melt index (MI₂) measured according to ASTM D1238 at 190° C. and 2.16 kg load, and the third ethylene-based component has a melt index (MI₃) measured according to ASTM D1238 at 190° C. and 2.16 kg load, and wherein the MI₁ is less than MI₂ and is also less than MI₃.
 4. The method of claim 3, wherein MI₁<MI₂<MI₃.
 5. The method of claim 1, wherein the first solution polymerization reactor is an adiabatic reactor.
 6. The method of claim 1, wherein one or more of the first solution polymerization reactor, the second solution polymerization reactor, and the third solution polymerization reactor comprise continuous stirred tank reactors, loop reactors, or combinations thereof.
 7. The method of claim 1, wherein the first solution polymerization reactor is an adiabatic continuous stirred tank reactor, and the second and third solution polymerization reactors are loop reactors.
 8. The method of claim 1, further comprising a tubular reactor downstream of the first solution polymerization reactor, the second solution polymerization reactor, and the third solution polymerization reactor, wherein the tubular reactor produces additional polymerization of the trimodal polymer.
 9. The method of claim 1, wherein the trimodal polymer has a density from 0.900 g/cc to 0.960 g/cc, and a melt index (I₂) of from 0.1 g/10 min. to 10.0 g/10 min.
 10. The method of claim 1, wherein the trimodal polymer comprises 2% to 45% by weight of the first ethylene-based component; 2% to 40% by weight of the second ethylene-based component; and 30% to 70% by weight of the third ethylene-based component.
 11. The method of claim 1, wherein the catalyst in the first solution polymerization reactor, the second solution polymerization reactor, or both is a catalyst according to Formula (I):

wherein M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4; n is 0, 1, or 2; when n is 1, X is a monodentate ligand or a bidentate ligand; when n is 2, each X is a monodentate ligand and is the same or different; the metal-ligand complex is overall charge-neutral; O is oxygen; each Z is independently chosen from —O—, —S—,—N(R^(N))—, or —P(R^(P))—; L is (C₁-C₄₀)hydrocarbylene or (C₁-C₄₀)heterohydrocarbylene, wherein the (C₁-C₄₀)hydrocarbylene has a portion that comprises a 1-carbon atom to 10-carbon atom linker backbone linking the two Z groups in Formula (I) (to which L is bonded) or the (C₁-C₄₀)heterohydrocarbylene has a portion that comprises a 1-atom to 10-atom linker backbone linking the two Z groups in Formula (I), wherein each of the 1 to 10 atoms of the 1-atom to 10-atom linker backbone of the (C₁-C₄₀)heterohydrocarbylene independently is a carbon atom or heteroatom, wherein each heteroatom independently is O, S, S(O), S(O)₂, Si(R^(C))₂, Ge(R^(C))₂, P(R^(C)), or N(R^(C)), wherein independently each R^(C) is (C₁-C₃₀)hydrocarbyl or (C₁-C₃₀)heterohydrocarbyl; R¹ and R⁸ are independently selected from the group consisting of (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, and radicals having Formula (II), Formula (III), or Formula (IV):

wherein in Formulas (II), (III), and (IV), each of R³¹⁻³⁵, R⁴¹⁻⁴⁸, or R⁵¹⁻⁵⁹ is independently chosen from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, or —H, provided at least one of R¹ or R⁸ is a radical having Formula (II), Formula (III), or Formula (IV); and wherein each of R²⁻⁴, R⁵⁻⁷, and R⁹⁻¹⁶ is independently selected from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂—OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(C))₂NC(O)—, halogen, and —H.
 12. The method of claim 1, wherein the catalyst in at least one of the first solution polymerization reactor, the second solution polymerization reactor, and the third solution polymerization reactor is a heterogeneous Ziegler-Natta catalyst. 13-15. (canceled)
 16. A method of producing a trimodal polymer in a solution polymerization process comprising: introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a first solution polymerization reactor to produce an effluent comprising a first ethylene-based component, wherein the first ethylene-based component has a density (ρ₁) of 0.870 to 0.910 g/cc, and a weight-average molecular weight (M_(w(GPC),1)) of 150 to 350 kg/mol as measured according to Gel Permeation Chromatography (GPC); introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to the second solution polymerization reactor to produce an effluent comprising a second ethylene-based component, wherein the second ethylene-based component has a density (ρ₂) from 0.895 to 0.925 g/cc, and a weight-average molecular weight (M_(w(GPC),2)) from 120 to 170 kg/mol; introducing at least one catalyst, ethylene monomer, at least one C₃-C₁₂ α-olefin comonomer, solvent, and optionally hydrogen to a third solution polymerization reactor to produce an effluent comprising a third ethylene-based component, wherein the third ethylene-based component has a density (ρ₃) of 0.920 to 0.980 g/cc, and a weight-average molecular weight (M_(w(GPC),3)) of 18 to 60 kg/mol; and mixing the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component to produce the trimodal polymer; wherein the first solution polymerization reactor or the third polymerization reactor is an adiabatic reactor; wherein different catalysts are used in the first solution polymerization reactor, the second polymerization reactor, and the third solution polymerization reactor; and wherein ρ₃>ρ₂>ρ₁, and M_(w(GPC),1)>M_(w(GPC),2)>M_(w(GPC),3).
 17. The method of claim 16, wherein the catalyst in at least one of the first solution polymerization reactor, the second solution polymerization reactor, and the third solution polymerization reactor is a heterogeneous Ziegler-Natta catalyst.
 18. The method of claim 16, wherein the first ethylene-based component is fed to the second solution polymerization reactor, the third solution polymerization reactor, or both.
 19. The method of claim 16, wherein the second ethylene-based component is fed to the first solution polymerization reactor, the third solution polymerization reactor, or both.
 20. The method of claim 16, wherein the third ethylene-based component is fed to the first solution polymerization reactor, the second solution polymerization reactor, or both.
 21. The method of claim 16, wherein the first ethylene-based component has a melt index (MI₁) measured according to ASTM D1238 at 190° C. and 2.16 kg load, the second ethylene-based component has a melt index (MI₂) measured according to ASTM D1238 at 190° C. and 2.16 kg load, and the third ethylene-based component has a melt index (MI₃) measured according to ASTM D1238 at 190° C. and 2.16 kg load, and wherein the MI₁ is less than MI₂ and is also less than MI₃.
 22. The method of claim 16, wherein the trimodal polymer has a density from 0.900 g/cc to 0.960 g/cc, and a melt index (I₂) of from 0.1 g/10 min. to 10.0 g/10 min.
 23. The method of claim 16, wherein the trimodal polymer comprises 2% to 45% by weight of the first ethylene-based component; 2% to 40% by weight of the second ethylene-based component; and 30% to 70% by weight of the third ethylene-based component.
 24. The method of claim 16, wherein the catalyst in the first solution polymerization reactor, the second solution polymerization reactor, or both is a catalyst according to Formula (I):

wherein M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4; n is 0, 1, or 2; when n is 1, X is a monodentate ligand or a bidentate ligand; when n is 2, each X is a monodentate ligand and is the same or different; the metal-ligand complex is overall charge-neutral; O is oxygen; each Z is independently chosen from —O—, —S—, —N(R^(N))—, or —P(R^(P))—; L is (C₁-C₄₀)hydrocarbylene or (C₁-C₄₀)heterohydrocarbylene, wherein the (C₁-C₄₀)hydrocarbylene has a portion that comprises a 1-carbon atom to 10-carbon atom linker backbone linking the two Z groups in Formula (I) (to which L is bonded) or the (C₁-C₄₀)heterohydrocarbylene has a portion that comprises a 1-atom to 10-atom linker backbone linking the two Z groups in Formula (I), wherein each of the 1 to 10 atoms of the 1-atom to 10-atom linker backbone of the (C₁-C₄₀)heterohydrocarbylene independently is a carbon atom or heteroatom, wherein each heteroatom independently is O, S, S(O), S(O)₂, Si(R^(C))₂, Ge(R^(C))₂, P(R^(C)), or N(R^(C)), wherein independently each R^(C) is (C₁-C₃₀)hydrocarbyl or (C₁-C₃₀)heterohydrocarbyl; R¹ and R⁸ are independently selected from the group consisting of (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, Si(R^(C))₃, Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, and radicals having Formula (II), Formula (III), or Formula (IV):

wherein in Formulas (II), (III), and (IV), each of R³¹⁻³⁵, R⁴¹⁻⁴⁸, or R⁵¹⁻⁵⁹ is independently chosen from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂, —OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(N))₂NC(O)—, halogen, or —H, provided at least one of R¹ or R⁸ is a radical having Formula (II), Formula (III), or Formula (IV); and wherein each of R²⁻⁴, R⁵⁻⁷, and R⁹⁻¹⁶ is independently selected from (C₁-C₄₀)hydrocarbyl, (C₁-C₄₀)heterohydrocarbyl, —Si(R^(C))₃, —Ge(R^(C))₃, —P(R^(P))₂, —N(R^(N))₂—OR^(C), —SR^(C), —NO₂, —CN, —CF₃, R^(C)S(O)—, R^(C)S(O)₂—, (R^(C))₂C═N—, R^(C)C(O)O—, R^(C)OC(O)—, R^(C)C(O)N(R^(N))—, (R^(C))₂NC(O)—, halogen, and —H. 